Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 PX11313-WH5G004 SABIC INNOVATIVE US
LNP™ KONDUIT™
Lighting applications、Electronic and Electrical、Plastic bag
Non chloro non bromine fl、heat conduction
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/PX11313-WH5G004 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C8 | ISO 180/1U | 23 kJ/m² |
| 23°C | ASTM D4812 | 330 J/m |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/PX11313-WH5G004 |
|---|---|---|---|
| tensile strength | 断裂 | ISO 527-2/5 | 108 Mpa |
| elongation | 断裂4 | ASTM D638 | 1.3 % |
| Tensile modulus | --3 | ASTM D638 | 13300 Mpa |
| Flexural modulus | 50.0 mm 跨距5 | ASTM D790 | 12500 Mpa |
| tensile strength | 断裂4 | ASTM D638 | 98.0 Mpa |
| bending strength | --6,7 | ISO 178 | 186 Mpa |
| Flexural modulus | --6 | ISO 178 | 13000 Mpa |
| bending strength | 屈服, 50.0 mm 跨距5 | ASTM D790 | 167 Mpa |
| Tensile modulus | -- | ISO 527-2/1 | 13300 Mpa |
| elongation | 断裂 | ISO 527-2/5 | 1.3 % |
| bending strength | 断裂, 50.0 mm 跨距5 | ASTM D790 | 176 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/PX11313-WH5G004 |
|---|---|---|---|
| Dissipation Factor | 1.10 GHz | ASTM ES7-83 | 9.9E-3 |
| Surface Resistivity | ASTM D257 | > 1.0E+15 ohms | |
| dielectric strength | 1.00 mm, in Oil | ASTM D149 | > 10 KV/mm |
| dielectric constant | 1.10 GHz | ASTM ES7-83 | 4.84 |
| Hot wire ignition (HWI) | UL 746 | PLC 3 | |
| High arc combustion index (HAI) | UL 746 | PLC 0 | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/PX11313-WH5G004 |
|---|---|---|---|
| Hot filament ignition temperature | 3.0 mm | IEC 60695-2-13 | 800 °C |
| UL flame retardant rating | 0.8 mm | UL 94 | V-0 |
| Hot filament ignition temperature | 1.0 mm | IEC 60695-2-13 | 750 °C |
| Burning wire flammability index | 1.0 到 3.0 mm | IEC 60695-2-12 | 960 °C |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/PX11313-WH5G004 |
|---|---|---|---|
| Shrinkage rate | 流动 : 24小时 | ASTM D955 | 0.42 % |
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.040 % |
| 24 hr, 23°C2 | ISO 62 | 0.23 % | |
| Shrinkage rate | 横向流动 : 24小时 | ASTM D955 | 0.58 % |
| Water absorption rate | 24 hr, 23°C | ISO 62 | 0.040 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/PX11313-WH5G004 |
|---|---|---|---|
| Heat distortion temperature | 0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距8，HDT | ISO 75-2/Bf | 228 °C |
| Linear coefficient of thermal expansion | 流动 : 40 到 120°C | ASTM E831 | 4.1E-5 cm/cm/°C |
| Heat distortion temperature | 0.45 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 227 °C |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距8，HDT | ISO 75-2/Af | 208 °C | |
| ball-indentation hardness | 123 到 127°C | IEC 60695-10-2 | 通过 |
| RTI | UL 746 | 120 °C | |
| Linear coefficient of thermal expansion | 横向 : 40 到 120°C | ASTM E831 | 8.5E-5 cm/cm/°C |
| thermal conductivity | --10 | ASTM E1461 | 1.8 W/m/K |
| --12 | ISO 22007-2 | 1.9 W/m/K | |
| --9 | ASTM E1461 | 1.4 W/m/K | |
| --11 | ISO 22007-2 | 0.90 W/m/K | |
| Heat distortion temperature | 1.8 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 215 °C |
| RTI Imp | UL 746 | 105 °C | |
| RTI Elec | UL 746 | 130 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE US/PX11313-WH5G004 |
|---|---|---|---|
| drying time | 4.0 hr | ||
| screw speed | 20 to 60 rpm | ||
| Suggested maximum moisture content | 0.15 to 0.25 % | ||
| Temperature in the middle of the barrel | 270 to 290 °C | ||
| Temperature at the rear of the barrel | 260 to 275 °C | ||
| Processing (melt) temperature | 270 to 295 °C | ||
| drying temperature | 80 °C | ||
| Temperature at the front of the material cylinder | 270 to 290 °C | ||
| Back pressure | 0.200 to 0.300 Mpa | ||
| Temperature | 85 to 100 °C |