Material Properties:Flame retardant｜Glass fiber reinforced｜High temperature resistance｜Glass fiber content 28.4%
Application Areas:Automotive External Parts｜Electrical applications
Color:--
Grade:--

Technical Data Sheet Compare

Mechanical properties	Test Method	Test Result
Tensile modulus	ISO 527	-- GPa
Impact strength of cantilever beam gap	ISO 180	-- kJ/m²
bending strength	ISO 178	226.6 Mpa
tensile strength	ISO 527	151.4 Mpa
elongation at break	ISO 527	5.3 %
Flexural modulus	ISO 178	10 GPa
Impact strength of simply supported beam without notch	ISO 179	52.4 kJ/m²
Charpy Notched Impact Strength	ISO 179	19.0 kJ/m²

Other performance	Test Condition	Test Method	Test Result
Shrinkage rate		-	-- %
Shrinkage rate	Shrinkage rate		-	-- %
UL flame retardant rating		UL 94	--
density		ISO 1183	-- g/cm³
Water absorption rate		ISO 62	-- %

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		IEC 93	-- Ω.cm
dielectric strength		IEC 243	-- KV/mm

Thermal performance	Test Method	Test Result
melt mass-flow rate	ISO 1133	-- g/10min
Linear coefficient of thermal expansion	ISO 11359	-- 10-5k
Heat distortion temperature	ISO 75	-- °C
melting temperature	ISO 3146	-- °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.