Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 27GFT HENAN SHENMA HUAWEI
--
Automotive External Parts、Electrical applications
Flame retardant、Glass fiber reinforced、High temperature resistan、Glass fiber content 28.4%
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | HENAN SHENMA HUAWEI/27GFT |
|---|---|---|---|
| Shrinkage rate | 平行，- | - | -- % |
| 垂直，- | - | -- % | |
| UL flame retardant rating | UL 94 | -- | |
| Water absorption rate | 23℃饱和 | ISO 62 | -- % |
| density | ISO 1183 | -- g/cm³ |
| Mechanical properties | Test Condition | Test Method | HENAN SHENMA HUAWEI/27GFT |
|---|---|---|---|
| Impact strength of cantilever beam gap | 干态 | ISO 180 | -- kJ/m² |
| Impact strength of simply supported beam without notch | 干态 | ISO 179 | 52.4 kJ/m² |
| elongation at break | 干态 | ISO 527 | 5.3 % |
| Charpy Notched Impact Strength | 干态 | ISO 179 | 19.0 kJ/m² |
| bending strength | 干态 | ISO 178 | 226.6 Mpa |
| Tensile modulus | 干态 | ISO 527 | -- GPa |
| tensile strength | 干态 | ISO 527 | 151.4 Mpa |
| Flexural modulus | 干态 | ISO 178 | 10 GPa |
| Electrical performance | Test Condition | Test Method | HENAN SHENMA HUAWEI/27GFT |
|---|---|---|---|
| dielectric strength | 干态 | IEC 243 | -- KV/mm |
| Volume resistivity | 干态/湿态 | IEC 93 | -- Ω.cm |
| Thermal performance | Test Condition | Test Method | HENAN SHENMA HUAWEI/27GFT |
|---|---|---|---|
| Heat distortion temperature | 1.80MPa，HDT | ISO 75 | -- °C |
| melting temperature | 干态 | ISO 3146 | -- °C |
| melt mass-flow rate | 干态 | ISO 1133 | -- g/10min |
| Linear coefficient of thermal expansion | ISO 11359 | -- 10-5k |