PP Daplen™ EE109AE BOREALIS EUROPE
192
- Unit Price:US$ 1,676 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:12.8MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Easy to process｜High impact resistance｜High rigidity｜filler｜Mineral filler｜20%｜Filler by weight
- Application Areas:Automotive External Parts｜Car bumper｜Automotive External Parts
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ball-indentation hardness | H132/10 | ISO 2039-1 | 26.0 Mpa |
| H132/10 | ISO 2039-1 | 26.0 Mpa |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | -- | ISO 306/A50 | 121 °C |
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 92.0 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 50.0 °C | |
| vicat | -- | ISO 306/B50 | 38.0 °C |
| Linear coefficient of thermal expansion | MD：-30到80°C | 内部方法 | 5E-05 cm/cm/°C |
| vicat | -- | ISO 306/A50 | 121 °C |
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 92.0 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 50.0 °C | |
| vicat | -- | ISO 306/B50 | 38.0 °C |
| Linear coefficient of thermal expansion | MD：-30到80°C | 内部方法 | 5E-05 cm/cm/°C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -20°C | ISO 179/1eU | 无断裂 |
| 23°C | ISO 179/1eU | 无断裂 | |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 4.2 kJ/m² |
| -20°C | ISO 179/1eA | 5.0 kJ/m² | |
| 23°C | ISO 179/1eA | 40 kJ/m² | |
| Impact strength of cantilever beam gap | -20°C | ISO 180/1A | 6.1 kJ/m² |
| 23°C | ISO 180/1A | 41 kJ/m² | |
| Impact strength of simply supported beam without notch | -20°C | ISO 179/1eU | 无断裂 |
| 23°C | ISO 179/1eU | 无断裂 | |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 4.2 kJ/m² |
| -20°C | ISO 179/1eA | 5.0 kJ/m² | |
| 23°C | ISO 179/1eA | 40 kJ/m² | |
| Impact strength of cantilever beam gap | -20°C | ISO 180/1A | 6.1 kJ/m² |
| 23°C | ISO 180/1A | 41 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | --2 | 内部方法 | 0.65 % |
| 90°C,2小时 | 内部方法 | 0.10 % | |
| melt mass-flow rate | 230°C/2.16kg | ISO 1133 | 13 g/10min |
| density | ISO 1183 | 1.04 g/cm³ | |
| shrinkage rate | --2 | 内部方法 | 0.65 % |
| 90°C,2小时 | 内部方法 | 0.10 % | |
| melt mass-flow rate | 230°C/2.16kg | ISO 1133 | 13 g/10min |
| density | ISO 1183 | 1.04 g/cm³ |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile strain | 断裂 | ISO 527-2/50 | >300 % |
| 屈服 | ISO 527-2/50 | 7.0 % | |
| bending strength | ISO 178 | 21.0 Mpa | |
| ISO 178 | 21.0 Mpa | ||
| flexural modulus | ISO 178 | 1500 Mpa | |
| Tensile modulus | ISO 527-2/1 | 1400 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 16.0 Mpa |
| Tensile strain | 断裂 | ISO 527-2/50 | >300 % |
| 屈服 | ISO 527-2/50 | 7.0 % | |
| bending strength | ISO 178 | 21.0 Mpa | |
| ISO 178 | 21.0 Mpa | ||
| flexural modulus | ISO 178 | 1500 Mpa | |
| Tensile modulus | ISO 527-2/1 | 1400 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 16.0 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.