Material Description

Material Properties:Dimensional stability｜High impact resistance｜Oil resistant
Application Areas:Automotive sector｜Industrial applications
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	23°C	ISO 179	5.6 kJ/m²
Impact strength of cantilever beam gap	-40°C	ASTM D256	45 J/m
	Impact strength of cantilever beam gap	23°C	ASTM D256	64 J/m
		Impact strength of cantilever beam gap	-40°C	ISO 180	4.0 kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180	5.5 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	23°C	ISO 527-2	3700 Mpa
tensile strength	Break,23°C	ASTM D638	85.0 Mpa
tensile strength	tensile strength	Break,23°C	ISO 527-2	85.0 Mpa
elongation	Break,23°C	ASTM D638	4.9 %
Tensile strain	Break,23°C	ISO 527-2	4.9 %
Bending modulus	23°C	ISO 178	3270 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	120 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	70.0 °C
Melting temperature		ASTM D3418	220 °C
Melting temperature	Melting temperature		ISO 3146	220 °C
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	195 °C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	160 °C

Physical properties	Test Condition	Test Method	Test Result
density		ASTM D792	1.36 g/cm³
density	density		ISO 1183	1.36 g/cm³
Shrinkage rate	MD：3.18mm		0.90 %
Water absorption rate	Saturation	ASTM D570	6.2 %
	Water absorption rate	Saturation,23°C	ISO 62	6.2 %
		Water absorption rate	Equilibrium,50%RH	ASTM D570	2.4 %
		Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	2.4 %

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity	1.50mm	ASTM D257	>1.0E+15 ohms·cm
Volume resistivity	Volume resistivity		IEC 60093	>1.0E+15 ohms·cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA6 Ultramid® B3M6 BASF GERMANY

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet