Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 B3M6 BASF GERMANY
Ultramid®
Automotive sector、Industrial applications
Dimensional stability、High impact resistance、Oil resistant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF GERMANY/B3M6 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 5.6 kJ/m² |
| Impact strength of cantilever beam gap | -40°C | ASTM D256 | 45 J/m |
| 23°C | ASTM D256 | 64 J/m | |
| 23°C | ISO 180 | 5.5 kJ/m² | |
| -40°C | ISO 180 | 4.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | BASF GERMANY/B3M6 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| 1.50mm | ASTM D257 | >1.0E+15 ohms·cm |
| Mechanical properties | Test Condition | Test Method | BASF GERMANY/B3M6 |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2 | 4.9 % |
| Flexural modulus | 23°C | ISO 178 | 3270 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 3700 Mpa |
| tensile strength | 断裂,23°C | ISO 527-2 | 85.0 Mpa |
| 断裂,23°C | ASTM D638 | 85.0 Mpa | |
| elongation | 断裂,23°C | ASTM D638 | 4.9 % |
| physical property | Test Condition | Test Method | BASF GERMANY/B3M6 |
|---|---|---|---|
| Shrinkage rate | MD：3.18mm | 0.90 % | |
| Water absorption rate | 饱和 | ASTM D570 | 6.2 % |
| 平衡,50%RH | ASTM D570 | 2.4 % | |
| 平衡,23°C,50%RH | ISO 62 | 2.4 % | |
| 饱和,23°C | ISO 62 | 6.2 % | |
| density | ASTM D792 | 1.36 g/cm³ | |
| ISO 1183 | 1.36 g/cm³ |
| Thermal performance | Test Condition | Test Method | BASF GERMANY/B3M6 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 120 °C |
| 0.45MPa,未退火，HDT | ASTM D648 | 195 °C | |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 160 °C | |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 70.0 °C | |
| melting temperature | ASTM D3418 | 220 °C | |
| ISO 3146 | 220 °C |