PBT CELANEX® 3300D CELANESE USA
223
- Unit Price:US$ 3,138 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:35MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Glass fiber reinforced｜Filler: Glass fiber reinforced material｜30% filler by weight
- Application Areas:Automotive sector｜currency
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO 294-4 | 0.30to0.70 % | ||
| Water absorption rate | ISO 62 | 0.20 % | |
| Vertical flow direction | ISO 294-4 | 0.70to1.1 % | |
| flow | ASTM D955 | 0.30to0.50 % | |
| melt mass-flow rate | ASTM D1238 | 16 g/10min | |
| density | ASTMD792 | 1.53 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ISO 2039-2 | 90 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Limiting Oxygen Index | ISO 4589-2 | 20 % | |
| UL flame retardant rating | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| -40°C | ASTM D638 | 11000 Mpa | |
| 0°C | ASTM D638 | 10500 Mpa | |
| bending strength | ISO 178 | 210 Mpa | |
| fracture | ISO 527-2/1A/5 | 2.5 % | |
| Flexural modulus | ISO 178 | 9700 Mpa | |
| Fracture, 121 ° C | ASTM D638 | 4.3 % | |
| Fracture, 80 ° C | ASTM D638 | 3.9 % | |
| Fracture, 0 ° C | ASTM D638 | 1.9 % | |
| Fracture, 23 ° C | ASTM D638 | 2.0 % | |
| Fracture, -40 ° C | ASTM D638 | 1.9 % | |
| 23°C | ASTM D638 | 9650 Mpa | |
| 80°C | ASTM D638 | 4830 Mpa | |
| 121°C | ASTM D638 | 3760 Mpa | |
| Fracture, -40 ° C | ASTM D638 | 190 Mpa | |
| Fracture, 0 ° C | ASTM D638 | 159 Mpa | |
| Fracture, 23 ° C | ASTM D638 | 134 Mpa | |
| Fracture, 80 ° C | ASTM D638 | 77.2 Mpa | |
| Fracture, 121 ° C | ASTM D638 | 61.4 Mpa | |
| fracture | ISO 527-2/1A/5 | 130 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | 8.5 kJ/m² | |
| ISO 179/1eA | 8.5 kJ/m² | ||
| Impact strength of simply supported beam without notch | ISO 179/1eU | 45 kJ/m² | |
| ISO 179/1eU | 46 kJ/m² | ||
| Impact strength of cantilever beam gap | ISO 180/1A | 7.5 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 1MHz | ASTMD150 | 0.016 | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V | |
| 100Hz | IEC 60250 | 2.2E-03 | |
| 1MHz | IEC 60250 | 4.10 | |
| ASTM D150 | 3.70 | ||
| 100Hz | IEC 60250 | 4.50 | |
| --3 | ASTM D149 | 22 KV/mm | |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | ISO 11359-2 | 2.5E-05 cm/cm/°C | |
| ISO 11359-2 | 1E-04 cm/cm/°C | ||
| melting temperature | ISO 11357-3 | 225 °C | |
| vicat | ISO 306/B50 | 220 °C | |
| Glass Transition Temperature | ISO 11357-2 | 60.0 °C | |
| 1.8MPa, Not annealed | ASTM D648 | 206 °C | |
| ISO 75-2/A | 205 °C | ||
| 8.0Mpa, Not annealed | ISO 75-2/C | 150 °C | |
| 0.45MPa, annealing | ASTM D648 | 228 °C | |
| 0.45MPa, Not annealed | ISO 75-2/B | 225 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.