Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 3300D CELANESE USA
CELANEX®
Automotive sector、currency
Glass fiber reinforced、Filler: Glass fiber reinf、30% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | CELANESE USA/3300D |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 8.5 kJ/m² |
| -30°C | ISO 179/1eA | 8.5 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 46 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 7.5 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 45 kJ/m² |
| hardness | Test Condition | Test Method | CELANESE USA/3300D |
|---|---|---|---|
| Rockwell hardness | M计秤 | ISO 2039-2 | 90 |
| Electrical performance | Test Condition | Test Method | CELANESE USA/3300D |
|---|---|---|---|
| 1MHz | 1MHz | IEC 60250 | 4.10 |
| 100Hz | 100Hz | IEC 60250 | 4.50 |
| 1MHz | 1MHz | ASTM D150 | 3.70 |
| --3 | ASTM D149 | 22 KV/mm | |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| 1MHz | 1MHz | ASTMD150 | 0.016 |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| Mechanical properties | Test Condition | Test Method | CELANESE USA/3300D |
|---|---|---|---|
| Fracture, 23 ° C | ASTM D638 | 134 Mpa | |
| Fracture, 0 ° C | 断裂,0°C | ASTM D638 | 1.9 % |
| 23°C | ASTM D638 | 9650 Mpa | |
| -40°C | -40℃ | ASTM D638 | 11000 Mpa |
| 80°C | 80℃ | ASTM D638 | 4830 Mpa |
| Fracture, 0 ° C | 断裂,0°C | ASTM D638 | 159 Mpa |
| 0°C | ASTM D638 | 10500 Mpa | |
| Fracture, 80 ° C | 断裂,80°C | ASTM D638 | 3.9 % |
| Fracture, -40 ° C | ASTM D638 | 1.9 % | |
| bending strength | 23°C | ISO 178 | 210 Mpa |
| Fracture, 121 ° C | 断裂,121°C | ASTM D638 | 4.3 % |
| Fracture, -40 ° C | ASTM D638 | 190 Mpa | |
| Flexural modulus | 23°C | ISO 178 | 9700 Mpa |
| fracture | ISO 527-2/1A/5 | 2.5 % | |
| Fracture, 80 ° C | 断裂,80°C | ASTM D638 | 77.2 Mpa |
| fracture | ISO 527-2/1A/5 | 130 Mpa | |
| 121°C | 121℃ | ASTM D638 | 3760 Mpa |
| Fracture, 23 ° C | ASTM D638 | 2.0 % | |
| Fracture, 121 ° C | 断裂,121°C | ASTM D638 | 61.4 Mpa |
| flammability | Test Condition | Test Method | CELANESE USA/3300D |
|---|---|---|---|
| UL flame retardant rating | 0.710mm | UL 94 | HB |
| Limiting Oxygen Index | ISO 4589-2 | 20 % |
| physical property | Test Condition | Test Method | CELANESE USA/3300D |
|---|---|---|---|
| 流动方向 | ISO 294-4 | 0.30to0.70 % | |
| Vertical flow direction | ISO 294-4 | 0.70to1.1 % | |
| density | ASTMD792 | 1.53 g/cm³ | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.20 % |
| flow | ASTM D955 | 0.30to0.50 % | |
| melt mass-flow rate | ASTM D1238 | 16 g/10min |
| Thermal performance | Test Condition | Test Method | CELANESE USA/3300D |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 225 °C | |
| 1.8MPa, Not annealed | ASTM D648 | 206 °C | |
| vicat | ISO 306/B50 | 220 °C | |
| 0.45MPa, annealing | ASTM D648 | 228 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 2.5E-05 cm/cm/°C |
| 1.8MPa, Not annealed | ISO 75-2/A | 205 °C | |
| 8.0Mpa, Not annealed | ISO 75-2/C | 150 °C | |
| 0.45MPa, Not annealed | ISO 75-2/B | 225 °C | |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 1E-04 cm/cm/°C |
| Glass Transition Temperature | ISO 11357-2 | 60.0 °C |