Material Description
- Material Properties:Flame retardant｜Bromine free｜Chlorine free｜Filler: Glass fiber reinforced material｜15% filler by weight
- Application Areas:Plastic bag｜Automotive External Parts
- Color:--
- Grade:--
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | R计秤 | ISO 2039-2 | 98 |
| ball-indentation hardness | H358/30 | ISO 2039-1 | 128 Mpa |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 0.45MPa, Unanealed, 3.20mm | ASTM D648 | 220 °C | |
| 0.45MPa, Unanealed, 64.0mm span | ISO 75-2/Bf | 220 °C | |
| 1.8MPa, Unanealed, 3.20mm | ASTM D648 | 200 °C | |
| 1.8MPa, Unanealed, 64.0mm span | ISO 75-2/Af | 200 °C | |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |
| Linear coefficient of thermal expansion | MD:-40到40°C | ISO 11359-2 | 2.9E-05 cm/cm/°C |
| MD:23到150°C | ISO 11359-2 | 4.2E-05 cm/cm/°C | |
| TD:-40到40°C | ISO 11359-2 | 7E-05 cm/cm/°C | |
| TD:23到150°C | ISO 11359-2 | 1.7E-04 cm/cm/°C | |
| RTI Imp | UL 746 | 120 °C | |
| RTI Elec | UL 746 | 140 °C | |
| RTI | UL 746 | 140 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.800mm | UL 94 | V-0 |
| Burning wire flammability index | 3.00mm | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | 3.00mm | IEC 60695-2-13 | 750 °C |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| filler | ASTM D229 | 15 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/2U | 25 kJ/m² |
| 23°C | ISO 179/2U | 35 kJ/m² | |
| -30°C | ASTM D256 | 50 J/m | |
| 0°C | ASTM D256 | 50 J/m | |
| 23°C | ASTM D256 | 50 J/m | |
| -30°C | ISO 180/1A | 6.0 kJ/m² | |
| 0°C | ISO 180/1A | 6.0 kJ/m² | |
| 23°C | ISO 180/1A | 6.0 kJ/m² | |
| -30°C | ASTM D4812 | 360 J/m | |
| 23°C | ASTM D4812 | 400 J/m | |
| -30°C | ISO 180/1U | 23 kJ/m² | |
| 23°C | ISO 180/1U | 30 kJ/m² |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt viscosity | 260°C,1500sec^-1 | ISO 11443 | 150 Pa·s |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | 饱和,23°C | ISO 62 | 0.15 % |
| 平衡,23°C,50%RH | ISO 62 | 0.070 % | |
| melt mass-flow rate | 265°C/5.0kg | ASTM D1238 | 24 g/10min |
| Melt volume flow rate | 250°C/5.0kg | ISO 1133 | 17.0 cm3/10min |
| 265°C/5.0kg | ISO 1133 | 18.0 cm3/10min | |
| shrinkage rate | MD1 | 内部方法 | 0.30-0.80 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| volume resistivity | ASTMD257 | 1E+15 ohms·cm | |
| 0.800mm, inoil | ASTM D149 | 28 KV/mm | |
| 16mm, inoyl | ASTM D149 | 21 KV/mm | |
| 3.20mm, inoil | ASTM D149 | 17 KV/mm | |
| 0.800mm, In oil | IEC 60243-1 | 28 KV/mm | |
| 1.60mm, In oil | IEC 60243-1 | 21 KV/mm | |
| 3.20mm, In oil | IEC 60243-1 | 17 KV/mm | |
| dielectric constant | 1MHz | ASTMD150 | 3.70 |
| Dissipation Factor | 1MHz | ASTMD150 | 0.15 |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| --2 | ASTM D638 | 7300 Mpa | |
| yield | ASTM D638 | 80.0 Mpa | |
| ISO 527-2/5 | 80.0 Mpa | ||
| fracture | ASTM D638 | 80.0 Mpa | |
| ISO 527-2/5 | 80.0 Mpa | ||
| yield | ASTM D638 | 2.0 % | |
| ISO 527-2/5 | 2.0 % | ||
| fracture | ASTM D638 | 3.0 % | |
| ISO 527-2/5 | 3.0 % | ||
| 50.0mm span | ASTM D790 | 5800 Mpa | |
| --8 | ISO 178 | 6400 Mpa | |
| --9 | ISO 178 | 130 Mpa | |
| Yield, 50.0mm span | ASTM D790 | 120 Mpa | |
| Fracture, 50.0mm span | ASTM D790 | 120 Mpa | |
| Fracture bending strain | ISO 178 | 3.0 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.