PBT ENH4530 SABIC INNOVATIVE NANSHA

VALOX™

Plastic bag,Automotive External Parts

Flame retardant,Bromine free,Chlorine free,Filler: Glass fiber reinf,15% filler by weight

--

--

--

--

--

--

--

--

--

--

--

--

--

--

--

Plastic Datasheets

hardness	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/ENH4530
Ball Pressure Test	H358/30	ISO 2039-1	128 Mpa
Rockwell hardness	R-Sale	ISO 2039-2	98

Supplementary Information	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/ENH4530
Filling material		ASTM D229	15 %

thermal performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/ENH4530
0.45MPa, unannealed, 3.20mm		ASTM D648	220 °C
0.45MPa, unannealed, 64.0mm span		ISO 75-2/Bf	220 °C
1.8MPa, unannealed, 3.20mm		ASTM D648	200 °C
1.8MPa, unannealed, 64.0mm span of		ISO 75-2/Af	200 °C
Ball Pressure Test	125°C	IEC 60695-10-2	Pass
Linear coefficient of thermal expansion	TD:-40to40°C	ISO 11359-2	7E-05 cm/cm/°C
		MD:23to150°C	ISO 11359-2	4.2E-05 cm/cm/°C
		TD:23to150°C	ISO 11359-2	1.7E-04 cm/cm/°C
		MD:-40to40°C	ISO 11359-2	2.9E-05 cm/cm/°C
RTI		UL 746	140 °C
RTI Elec		UL 746	140 °C
RTI Imp		UL 746	120 °C

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/ENH4530
--2		ASTM D638	7300 Mpa
50.0mm span		ASTM D790	5800 Mpa
--8		ISO 178	6400 Mpa
--9		ISO 178	130 Mpa
crack		ASTM D638	80.0 Mpa
			ISO 527-2/5	80.0 Mpa
			ASTM D638	3.0 %
			ISO 527-2/5	3.0 %
Fracture, 50.0mm span		ASTM D790	120 Mpa
Fracture bending strain		ISO 178	3.0 %
yield		ASTM D638	2.0 %
			ISO 527-2/5	2.0 %
			ASTM D638	80.0 Mpa
			ISO 527-2/5	80.0 Mpa
Yield, 50.0mm span		ASTM D790	120 Mpa

Electrical performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/ENH4530
0.800mm,inOil		ASTM D149	28 KV/mm
0.800mm, in oil		IEC 60243-1	28 KV/mm
1.60mm,inOil		ASTM D149	21 KV/mm
1.60mm, in oil		IEC 60243-1	21 KV/mm
3.20mm, inoil		ASTM D149	17 KV/mm
3.20mm, in oil		IEC 60243-1	17 KV/mm
Dielectric constant	1MHz	ASTMD150	3.70
Dissipation factor	1MHz	ASTMD150	0.15
Surface resistivity		IEC 60093	>1.0E+15 ohms
Volume resistivity		ASTMD257	1E+15 ohms·cm

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/ENH4530
melt mass-flow rate	265°C/5.0kg	ASTM D1238	24 g/10min
Melt Volume Flow Rate (MVR)	265°C/5.0kg	ISO 1133	18.0 cm3/10min
Melt Volume Flow Rate (MVR)		250°C/5.0kg	ISO 1133	17.0 cm3/10min
Shrinkage rate	MD1	Internal Method	0.30-0.80 %
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.070 %
Water absorption rate		Saturation,23°C	ISO 62	0.15 %

impact performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/ENH4530
0°C		ISO 180/1A	6.0 kJ/m²
0°C			ASTM D256	50 J/m
23°C		ASTM D256	50 J/m
			ASTM D4812	400 J/m
			ISO 180/1U	30 kJ/m²
			ISO 180/1A	6.0 kJ/m²
-30°C		ASTM D4812	360 J/m
			ASTM D256	50 J/m
			ISO 180/1A	6.0 kJ/m²
			ISO 180/1U	23 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/2U	35 kJ/m²
Impact strength of simply supported beam without notch		-30°C	ISO 179/2U	25 kJ/m²

flammability	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/ENH4530
Burning wire flammability index	3.00mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	3.00mm	IEC 60695-2-13	750 °C
UL flame retardant rating	0.800mm	UL 94	V-0

Filling analysis	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/ENH4530
Melt viscosity	260°C,1500sec^-1	ISO 11443	150 Pa·s