Material Description
- Material Properties:Low viscosity|transparent
- Application Areas:building materials|Profile
- Color:--
- Grade:Injection grade
Material Certification

Technical Data Sheet
optical performance | Test Condition | Test Method | Test Result |
---|---|---|---|
Refractive index | ISO 489 | 1.586 | |
transmissivity | 2540 μm | ASTM D1003 | 88.0 to 90.0 % |
turbidity | 2540 μm | ASTM D1003 | < 0.80 % |
impact performance | Test Condition | Test Method | Test Result |
---|---|---|---|
Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
23°C | ISO 179/1eU | 无断裂 | |
Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 11 kJ/m² |
23°C | ISO 180/1A | 65 kJ/m² | |
Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 无断裂 |
23°C | ISO 180/1U | 无断裂 |
flammability | Test Condition | Test Method | Test Result |
---|---|---|---|
UL flame retardant rating | 0.70 mm | UL 94 | HB |
3.0 mm | UL 94 | HB | |
Burning wire flammability index | 1.0 mm | IEC 60695-2-12 | 850 °C |
Extreme Oxygen Index | ISO 4589-2 | 25 % |
mechanical properties | Test Condition | Test Method | Test Result |
---|---|---|---|
Tensile modulus | ISO 527-2/1 | 2350 Mpa | |
tensile strength | Yield | ISO 527-2/50 | 63.0 Mpa |
Break | ISO 527-2/50 | 65.0 Mpa | |
Tensile strain | Yield | ISO 527-2/50 | 6.0 % |
Break | ISO 527-2/50 | 100 % | |
Bending modulus | ISO 178 | 2300 Mpa | |
bending strength | ISO 178 | 90.0 Mpa | |
Taber abraser | 1000 Cycles, 1000 g, CS-17 Wheel | Internal Method | 10.0 mg |
injection | Test Condition | Test Method | Test Result |
---|---|---|---|
drying temperature | 120 °C | ||
drying time | 2.0 to 4.0 hr | ||
Suggested maximum moisture content | 0.020 % | ||
Hopper temperature | 60 to 80 °C | ||
Temperature at the rear of the barrel | 260 to 280 °C | ||
Temperature in the middle of the barrel | 270 to 290 °C | ||
Temperature at the front of the material cylinder | 280 to 300 °C | ||
Spray nozzle temperature | 270 to 290 °C | ||
Processing (melt) temperature | 280 to 300 °C | ||
Mold temperature | 80 to 100 °C |
thermal performance | Test Condition | Test Method | Test Result |
---|---|---|---|
Hot deformation temperature | 0.45 MPa, Unannealed, 4.00 mm, 100 mm Span | ISO 75-2/Be | 133 °C |
1.8 MPa, Unannealed, 4.00 mm, 100 mm Span | ISO 75-2/Ae | 122 °C | |
Vicat softening temperature | -- | ISO 306/B50 | 140 °C |
-- | ISO 306/B120 | 141 °C | |
Ball Pressure Test | 123 to 127°C | IEC 60695-10-2 | 通过 |
Linear coefficient of thermal expansion | 23 to 80°C,Across Flow | ISO 11359-2 | 7.0E-5 cm/cm/°C |
thermal conductivity | ISO 8302 | 0.20 W/m/K | |
RTI Elec | UL 746 | 130 °C | |
RTI Imp | UL 746 | 125 °C | |
RTI | UL 746 | 125 °C |
Physical properties | Test Condition | Test Method | Test Result |
---|---|---|---|
Melt Volume Flow Rate (MVR) | 300°C/1.2 kg | ISO 1133 | 21.0 cm3/10min |
Shrinkage rate | Flow | Internal Method | 0.50 - 0.70 % |
Water absorption rate | Saturation, 23°C | ISO 62 | 0.35 % |
Equilibrium, 23°C, 50% RH | ISO 62 | 0.15 % |
Electrical performance | Test Condition | Test Method | Test Result |
---|---|---|---|
Surface resistivity | IEC 60093 | > 1.0E+15 ohms | |
Volume resistivity | IEC 60093 | > 1.0E+15 ohms·cm | |
Dielectric strength | 0.800 mm, in Oil | IEC 60243-1 | 35 KV/mm |
1.60 mm, in Oil | IEC 60243-1 | 27 KV/mm | |
3.20 mm, in Oil | IEC 60243-1 | 17 KV/mm | |
Relative permittivity | 50 Hz | IEC 60250 | 2.70 |
60 Hz | IEC 60250 | 2.70 | |
1 MHz | IEC 60250 | 2.70 | |
Dissipation factor | 50 Hz | IEC 60250 | 1.0E-3 |
60 Hz | IEC 60250 | 1.0E-3 | |
1 MHz | IEC 60250 | 0.010 |
hardness | Test Condition | Test Method | Test Result |
---|---|---|---|
Ball Pressure Test | H 358/30 | ISO 2039-1 | 95.0 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.