Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 121R-111 SABIC INNOVATIVE SPAIN
LEXAN™ 
building materials、Profile
Low viscosity、transparent
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE SPAIN/121R-111
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
23°CISO 179/1eU无断裂
Impact strength of cantilever beam gap-30°CISO 180/1A11 kJ/m²
Suspended wall beam without notch impact strength23°CISO 180/1U无断裂
Impact strength of cantilever beam gap23°CISO 180/1A65 kJ/m²
Suspended wall beam without notch impact strength-30°CISO 180/1U无断裂
hardnessTest ConditionTest MethodSABIC INNOVATIVE SPAIN/121R-111
ball-indentation hardnessH 358/30ISO 2039-195.0 Mpa
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE SPAIN/121R-111
Tensile modulusISO 527-2/12350 Mpa
tensile strength 屈服ISO 527-2/5063.0 Mpa
bending strengthISO 17890.0 Mpa
Flexural modulusISO 1782300 Mpa
Taber abraser1000 Cycles, 1000 g, CS-17 转轮内部方法10.0 mg
Tensile strain断裂ISO 527-2/50100 %
屈服ISO 527-2/506.0 %
tensile strength 断裂ISO 527-2/5065.0 Mpa
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE SPAIN/121R-111
dielectric strength1.60 mm, 在油中IEC 60243-127 KV/mm
relative permittivity50 HzIEC 602502.70
Dissipation Factor1 MHzIEC 602500.010
Volume resistivityIEC 60093> 1.0E+15 ohms·cm
dielectric strength0.800 mm, 在油中IEC 60243-135 KV/mm
Dissipation Factor60 HzIEC 602501.0E-3
relative permittivity1 MHzIEC 602502.70
Dissipation Factor50 HzIEC 602501.0E-3
Surface ResistivityIEC 60093> 1.0E+15 ohms
dielectric strength3.20 mm, 在油中IEC 60243-117 KV/mm
relative permittivity60 HzIEC 602502.70
optical performance Test ConditionTest MethodSABIC INNOVATIVE SPAIN/121R-111
transmissivity2540 µmASTM D100388.0 to 90.0 %
refractive indexISO 4891.586
Haze ratio2540 µmASTM D1003< 0.80 %
flammabilityTest ConditionTest MethodSABIC INNOVATIVE SPAIN/121R-111
UL flame retardant rating0.70 mmUL 94HB
3.0 mmUL 94HB
Burning wire flammability index1.0 mmIEC 60695-2-12850 °C
Limiting Oxygen IndexISO 4589-225 %
physical property Test ConditionTest MethodSABIC INNOVATIVE SPAIN/121R-111
Water absorption rate平衡, 23°C, 50% RHISO 620.15 %
Melt volume flow rate300°C/1.2 kgISO 113321.0 cm3/10min
Shrinkage rateFlow内部方法0.50 - 0.70 %
Water absorption rate饱和, 23°CISO 620.35 %
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE SPAIN/121R-111
vicat--ISO 306/B120141 °C
thermal conductivityISO 83020.20 W/m/K
Heat distortion temperature0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距，HDTISO 75-2/Be133 °C
1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距，HDTISO 75-2/Ae122 °C
vicat--ISO 306/B50140 °C
RTI ImpUL 746125 °C
ball-indentation hardness123 到 127°CIEC 60695-10-2通过
Linear coefficient of thermal expansion23 到 80°C，横向ISO 11359-27.0E-5 cm/cm/°C
RTIUL 746125 °C
RTI ElecUL 746130 °C
injectionTest ConditionTest MethodSABIC INNOVATIVE SPAIN/121R-111
drying time2.0 to 4.0 hr
Suggested maximum moisture content0.020 %
Temperature in the middle of the barrel270 to 290 °C
Temperature at the rear of the barrel260 to 280 °C
Processing (melt) temperature280 to 300 °C
Hopper temperature60 to 80 °C
drying temperature120 °C
Temperature at the front of the material cylinder280 to 300 °C
Temperature80 to 100 °C
Spray nozzle temperature270 to 290 °C