ASA/PC GELOY™ XP4034 SABIC INNOVATIVE US
432
- Unit Price:US$ 2,782 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:80MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
- Material Comparison:
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High mobility｜Thermal stability｜Antistatic｜Weather resistance
- Application Areas:Automotive sector
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | R-Scale | ASTM D785 | 110 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, Unannealed, 3.20 mm | ASTM D648 | 115 °C |
| 0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span7 | ISO 75-2/Bf | 116 °C | |
| 1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 104 °C | |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span7 | ISO 75-2/Af | 98.0 °C | |
| Vicat softening temperature | ISO 306/B50 | 113 °C | |
| Linear coefficient of thermal expansion | Flow : -20 to 150°C | ASTM E831 | 7.2E-5 cm/cm/°C |
| Across Flow : -20 to 150°C | ASTM E831 | 7.2E-5 cm/cm/°C | |
| thermal conductivity | ASTM C177 | 0.25 W/m/K |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | HB |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| gloss | 60°, 无织构 | ASTM D523 | 94 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 220°C/10.0 kg | ASTM D1238 | 5.0 g/10 min |
| 260°C/5.0 kg | ASTM D1238 | 14 g/10 min | |
| 280°C/3.8 kg | ASTM D1238 | 24 g/10 min | |
| Shrinkage rate | Flow : 3.20 mm | Internal Method | 0.50 - 0.70 % |
| Across FlowFlow : 3.20 mm | Internal Method | 0.50 - 0.70 % | |
| Water absorption rate | 24 hr | ASTM D570 | 0.25 % |
| Outdoor applicability | UL 746C | f2 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 95 to 105 °C | ||
| drying time | 3.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.040 % | ||
| Suggested injection volume | 40 to 80 % | ||
| Temperature at the rear of the barrel | 240 to 255 °C | ||
| Temperature in the middle of the barrel | 245 to 260 °C | ||
| Temperature at the front of the material cylinder | 250 to 265 °C | ||
| Spray nozzle temperature | 245 to 265 °C | ||
| Processing (melt) temperature | 260 to 275 °C | ||
| Mold temperature | 55 to 70 °C | ||
| Back pressure | 0.300 to 1.00 Mpa | ||
| Screw speed | 30 to 80 rpm | ||
| Exhaust hole depth | 0.038 to 0.076 mm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2500 Mpa | |
| tensile strength | Yield2 | ASTM D638 | 62.0 Mpa |
| Yield | ISO 527-2/50 | 57.0 Mpa | |
| Break | ISO 527-2/50 | 50.0 Mpa | |
| Tensile strain | Yield | ISO 527-2/50 | 4.5 % |
| Break2 | ASTM D638 | 25 % | |
| Break | ISO 527-2/50 | 130 % | |
| Bending modulus | 50.0 mm Span3 | ASTM D790 | 2510 Mpa |
| --4 | ISO 178 | 2500 Mpa | |
| bending strength | --4,5 | ISO 178 | 75.0 Mpa |
| Yield, 50.0 mm Span3 | ASTM D790 | 88.0 Mpa |
| impact performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dart impact | -30°C, Total Energy | ASTM D3763 | 30.0 J |
| 23°C, Total Energy | ASTM D3763 | 47.0 J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.