Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ASA/PC XP4034 SABIC INNOVATIVE US
GELOY™
Automotive sector
High mobility、Thermal stability、Antistatic、Weather resistance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/XP4034 |
|---|---|---|---|
| Dart impact | -30°C, Total Energy | ASTM D3763 | 30.0 J |
| 23°C, Total Energy | ASTM D3763 | 47.0 J |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE US/XP4034 |
|---|---|---|---|
| Rockwell hardness | R 级 | ASTM D785 | 110 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/XP4034 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2500 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 57.0 Mpa |
| 屈服2 | ASTM D638 | 62.0 Mpa | |
| Tensile strain | 断裂2 | ASTM D638 | 25 % |
| Flexural modulus | --4 | ISO 178 | 2500 Mpa |
| bending strength | 屈服, 50.0 mm 跨距3 | ASTM D790 | 88.0 Mpa |
| Tensile strain | 断裂 | ISO 527-2/50 | 130 % |
| bending strength | --4,5 | ISO 178 | 75.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2/50 | 4.5 % |
| Flexural modulus | 50.0 mm 跨距3 | ASTM D790 | 2510 Mpa |
| tensile strength | 断裂 | ISO 527-2/50 | 50.0 Mpa |
| optical performance | Test Condition | Test Method | SABIC INNOVATIVE US/XP4034 |
|---|---|---|---|
| gloss | 60°, 无织构 | ASTM D523 | 94 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/XP4034 |
|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | HB |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/XP4034 |
|---|---|---|---|
| melt mass-flow rate | 220°C/10.0 kg | ASTM D1238 | 5.0 g/10 min |
| Shrinkage rate | 横向流动 : 3.20 mm | 内部方法 | 0.50 - 0.70 % |
| Outdoor applicability | UL 746C | f2 | |
| Water absorption rate | 24 hr | ASTM D570 | 0.25 % |
| melt mass-flow rate | 280°C/3.8 kg | ASTM D1238 | 24 g/10 min |
| Shrinkage rate | 流动 : 3.20 mm | 内部方法 | 0.50 - 0.70 % |
| melt mass-flow rate | 260°C/5.0 kg | ASTM D1238 | 14 g/10 min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/XP4034 |
|---|---|---|---|
| Heat distortion temperature | 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距7，HDT | ISO 75-2/Af | 98.0 °C |
| Linear coefficient of thermal expansion | 流动 : -20 到 150°C | ASTM E831 | 7.2E-5 cm/cm/°C |
| thermal conductivity | ASTM C177 | 0.25 W/m/K | |
| Linear coefficient of thermal expansion | 横向 : -20 到 150°C | ASTM E831 | 7.2E-5 cm/cm/°C |
| vicat | ISO 306/B50 | 113 °C | |
| Heat distortion temperature | 0.45 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 115 °C |
| 1.8 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 104 °C | |
| 0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距7，HDT | ISO 75-2/Bf | 116 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE US/XP4034 |
|---|---|---|---|
| screw speed | 30 to 80 rpm | ||
| Suggested maximum moisture content | 0.040 % | ||
| Processing (melt) temperature | 260 to 275 °C | ||
| drying temperature | 95 to 105 °C | ||
| Suggested injection volume | 40 to 80 % | ||
| drying time | 3.0 to 4.0 hr | ||
| Temperature in the middle of the barrel | 245 to 260 °C | ||
| Temperature at the rear of the barrel | 240 to 255 °C | ||
| Exhaust hole depth | 0.038 to 0.076 mm | ||
| Temperature at the front of the material cylinder | 250 to 265 °C | ||
| Back pressure | 0.300 to 1.00 Mpa | ||
| Temperature | 55 to 70 °C | ||
| Spray nozzle temperature | 245 to 265 °C |