PC/PBT

PC/PBT XENOY™ 1760T SABIC INNOVATIVE US

303

Unit Price:US$ 3,005 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
53MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Chemical resistance｜High mobility｜Glass fiber reinforced｜High impact resistance｜Filler: Glass fiber reinforced material｜11% filler by weight
Application Areas:Automotive External Parts｜Phone case｜Shell
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	30 kJ/m²
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	3.5 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	4.0 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	35 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	35 kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	3.0 kJ/m²
	Impact strength of cantilever beam gap	0°C	ISO 180/1A	3.0 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	3.0 kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	30 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.50mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2/1	4500 Mpa
tensile strength	Break	ISO 527-2/5	90.0 Mpa
Tensile strain	Break	ISO 527-2/5	3.0 %
Bending modulus		ISO 178	4000 Mpa
bending strength		ISO 178	140 Mpa

thermal performance	Test Condition	Test Method	Test Result
0.45MPa, unannealed, 100mm span		ISO 75-2/Be	115 °C
1.8MPa, unannealed, 100mm span		ISO 75-2/Ae	105 °C
Ball Pressure Test	75°C	IEC 60695-10-2	Pass
Linear coefficient of thermal expansion	MD:23to80°C	ISO 11359-2	4E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:23to80°C	ISO 11359-2	1.1E-04 cm/cm/°C
thermal conductivity		ISO 8302	0.19 W/m/K

Physical properties	Test Condition	Test Method	Test Result
density		ISO 1183	1.30 g/cm³
Melt Volume Flow Rate (MVR)	250°C/5.0kg	ISO 1133	14.0 cm3/10min
Shrinkage rate	MD1	Internal Method	0.50-0.90 %
Water absorption rate	Saturation,23°C	ISO 62	0.50 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.15 %

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		IEC 60093	>1.0E+14 ohms·cm
Dielectric strength	3.20mm,in Oil	IEC 60243-1	17 KV/mm
Relative permittivity	50Hz	IEC 60250	3.30
	Relative permittivity	60Hz	IEC 60250	3.30
	Relative permittivity	Relative permittivity	1MHz	IEC 60250	3.10
Dissipation factor	50Hz	IEC 60250	2E-03
	Dissipation factor	60Hz	IEC 60250	2E-03
	Dissipation factor	Dissipation factor	1MHz	IEC 60250	0.020
Surface resistivity		IEC 60093	>1.0E+15 ohms

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Sale	ISO 2039-2	113
Ball Pressure Test	H358/30	ISO 2039-1	105 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC/PBT XENOY™ 1760T SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet