PPO

PPO NORYL™ PVX0901 BK1066 SABIC INNOVATIVE SHANGHAI

221

Unit Price:US$ 4,043 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High temperature resistance｜Hydrolysis resistance｜wear resistant
Application Areas:Home appliance components｜office equipment ｜Automotive Applications｜currency
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Dart impact	23°C,TotalEnergy	ASTM D3763	37.0 J
Charpy Notched Impact Strength	23°C	ISO 179/1eA	12 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5mm	UL 94	V-1

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	--	ISO 527-2/1	2440 Mpa
tensile strength	Yield4	ASTM D638	60.0 Mpa
Tensile modulus	--3	ASTM D638	2500 Mpa
bending strength	Yield,50.0mmSpan5	ASTM D790	86.0 Mpa
bending strength	bending strength	--6,7	ISO 178	95.0 Mpa
Bending modulus	--6	ISO 178	2450 Mpa
Bending modulus	Bending modulus	50.0mmSpan5	ASTM D790	2300 Mpa
elongation	Break	ISO 527-2/50	8.8 %
elongation	elongation	Break4	ASTM D638	6.6 %
tensile strength	Yield	ISO 527-2/50	59.0 Mpa
	tensile strength	Break4	ASTM D638	45.0 Mpa
	tensile strength	tensile strength	Break	ISO 527-2/50	44.0 Mpa
elongation	Yield4	ASTM D638	3.3 %
elongation	elongation	Yield	ISO 527-2/50	3.3 %

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	TD:-40to40°C	ISO 11359-2	7.8E-05 cm/cm/°C
	Linear coefficient of thermal expansion	TD:-40to40°C	ASTME831	8.1E-05 cm/cm/°C
		Linear coefficient of thermal expansion	MD:-40to40°C	ISO 11359-2	7.4E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD:-40to40°C	ASTME831	7.5E-05 cm/cm/°C
Vicat softening temperature	--	ISO 306/B120	109 °C
Vicat softening temperature	Vicat softening temperature	--	ASTMD152511	116 °C
Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan10	ISO 75-2/Af	89.0 °C
	Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	92.0 °C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	92.0 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.040 %
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	0.24 %
Shrinkage rate	MD：3.20mm	Internal Method	0.50-0.70 %
Melt Volume Flow Rate (MVR)	280°C/5.0kg	ISO 1133	52.0 cm3/10min
melt mass-flow rate	280°C/5.0kg	ASTM D1238	50 g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PPO NORYL™ PVX0901 BK1066 SABIC INNOVATIVE SHANGHAI

Material Description

Technical Data Sheet Compare

Technical Data Sheet