PPO PVX0901 BK1066 SABIC INNOVATIVE SHANGHAI
NORYL™
Home appliance components,office equipment ,Automotive Applications,currency
High temperature resistan,Hydrolysis resistance,wear resistant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/PVX0901 BK1066 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 12 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 37.0 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/PVX0901 BK1066 |
|---|---|---|---|
| elongation | 断裂4 | ASTM D638 | 6.6 % |
| bending strength | 屈服,50.0mm跨距5 | ASTM D790 | 86.0 Mpa |
| tensile strength | 屈服4 | ASTM D638 | 60.0 Mpa |
| Tensile modulus | --3 | ASTM D638 | 2500 Mpa |
| elongation | 断裂 | ISO 527-2/50 | 8.8 % |
| Flexural modulus | 50.0mm跨距5 | ASTM D790 | 2300 Mpa |
| bending strength | --6,7 | ISO 178 | 95.0 Mpa |
| Flexural modulus | --6 | ISO 178 | 2450 Mpa |
| tensile strength | 断裂 | ISO 527-2/50 | 44.0 Mpa |
| 屈服 | ISO 527-2/50 | 59.0 Mpa | |
| elongation | 屈服 | ISO 527-2/50 | 3.3 % |
| 屈服4 | ASTM D638 | 3.3 % | |
| tensile strength | 断裂4 | ASTM D638 | 45.0 Mpa |
| Tensile modulus | -- | ISO 527-2/1 | 2440 Mpa |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/PVX0901 BK1066 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | V-1 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/PVX0901 BK1066 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.70 % |
| melt mass-flow rate | 280°C/5.0kg | ASTM D1238 | 50 g/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.040 % |
| 饱和,23°C | ISO 62 | 0.24 % | |
| Melt volume flow rate | 280°C/5.0kg | ISO 1133 | 52.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/PVX0901 BK1066 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 92.0 °C |
| vicat | -- | ISO 306/B120 | 109 °C |
| Linear coefficient of thermal expansion | MD:-40到40°C | ISO 11359-2 | 7.4E-05 cm/cm/°C |
| TD:-40到40°C | ASTME831 | 8.1E-05 cm/cm/°C | |
| vicat | -- | ASTMD152511 | 116 °C |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 92.0 °C |
| 1.8MPa,未退火,64.0mm跨距10，HDT | ISO 75-2/Af | 89.0 °C | |
| Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 7.5E-05 cm/cm/°C |
| TD:-40到40°C | ISO 11359-2 | 7.8E-05 cm/cm/°C |