PBT VALOX™ 325FC-1001 SABIC INNOVATIVE SHANGHAI
205
- Unit Price:US$ 3,769 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:33MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Easy to process
- Application Areas:Industrial applications｜Automotive External Parts｜Outdoor applications｜Electrical appliances｜Construction field
- Color:--
- Grade:--
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | R计秤 | ISO 2039-2 | 117 |
| ball-indentation hardness | H358/30 | ISO 2039-1 | 145 Mpa |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 0.45MPa, Unanealed, 64.0mm span | ISO 75-2/Bf | 150 °C | |
| 1.8MPa, Unanealed, 64.0mm span | ISO 75-2/Af | 50.0 °C | |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 0°C | ISO 180/1A | 4.0 kJ/m² | |
| 23°C | ISO 180/1A | 4.0 kJ/m² | |
| -30°C | ASTM D4812 | 无断裂 | |
| 23°C | ASTMD4812 | 无断裂 | |
| -30°C | ISO 180/1U | 100 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/2U | 80 kJ/m² |
| 23°C | ISO 179/2U | 无断裂 | |
| -30°C | ASTM D256 | 36 J/m | |
| 0°C | ASTM D256 | 36 J/m | |
| 23°C | ASTM D256 | 38 J/m | |
| -30°C | ISO 180/1A | 4.0 kJ/m² |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt viscosity | 260°C,1500sec^-1 | ISO 11443 | 165 Pa·s |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt volume flow rate | 250°C/2.16kg | ISO 1133 | 20.0 cm3/10min |
| 250°C/5.0kg | ISO 1133 | 50.0 cm3/10min | |
| shrinkage rate | MD | 内部方法 | 2.0-2.6 % |
| TD | 内部方法 | 0.90-1.8 % | |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.34 % |
| 平衡,23°C,50%RH | ISO 62 | 0.080 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| --2 | ASTM D638 | 2500 Mpa | |
| yield | ASTM D638 | 60.0 Mpa | |
| ISO 527-2/50 | 60.0 Mpa | ||
| fracture | ASTM D638 | 60.0 Mpa | |
| ISO 527-2/50 | 60.0 Mpa | ||
| yield | ASTM D638 | 7.0 % | |
| ISO 527-2/50 | 10 % | ||
| fracture | ASTM D638 | 15 % | |
| ISO 527-2/50 | 15 % | ||
| flexural modulus | ISO 178 | 2400 Mpa | |
| bending strength | ISO 178 | 85.0 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.