Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 325FC-1001 SABIC INNOVATIVE SHANGHAI
VALOX™
Industrial applications、Automotive External Parts、Outdoor applications、Electrical appliances、Construction field
Easy to process
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/325FC-1001 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/2U | 无断裂 |
| 23°C | ISO 180/1A | 4.0 kJ/m² | |
| 0°C | ASTM D256 | 36 J/m | |
| 23°C | ASTMD4812 | 无断裂 | |
| -30°C | ASTM D4812 | 无断裂 | |
| 23°C | ASTM D256 | 38 J/m | |
| -30°C | ASTM D256 | 36 J/m | |
| ISO 180/1A | 4.0 kJ/m² | ||
| 0°C | ISO 180/1A | 4.0 kJ/m² | |
| -30°C | ISO 180/1U | 100 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/2U | 80 kJ/m² |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/325FC-1001 |
|---|---|---|---|
| Rockwell hardness | R计秤 | ISO 2039-2 | 117 |
| ball-indentation hardness | H358/30 | ISO 2039-1 | 145 Mpa |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/325FC-1001 |
|---|---|---|---|
| fracture | ISO 527-2/50 | 15 % | |
| --2 | ASTM D638 | 2500 Mpa | |
| yield | ASTM D638 | 60.0 Mpa | |
| ASTM D638 | 7.0 % | ||
| fracture | ASTM D638 | 15 % | |
| yield | ISO 527-2/50 | 60.0 Mpa | |
| ISO 527-2/50 | 10 % | ||
| bending strength | ISO 178 | 85.0 Mpa | |
| Flexural modulus | ISO 178 | 2400 Mpa | |
| fracture | ISO 527-2/50 | 60.0 Mpa | |
| ASTM D638 | 60.0 Mpa |
| Filling analysis | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/325FC-1001 |
|---|---|---|---|
| melt viscosity | 260°C,1500sec^-1 | ISO 11443 | 165 Pa·s |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/325FC-1001 |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 2.0-2.6 % |
| Melt volume flow rate | 250°C/5.0kg | ISO 1133 | 50.0 cm3/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.080 % |
| 饱和,23°C | ISO 62 | 0.34 % | |
| Shrinkage rate | TD | 内部方法 | 0.90-1.8 % |
| Melt volume flow rate | 250°C/2.16kg | ISO 1133 | 20.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/325FC-1001 |
|---|---|---|---|
| 0.45MPa, Unanealed, 64.0mm span | ISO 75-2/Bf | 150 °C | |
| 1.8MPa, Unanealed, 64.0mm span | ISO 75-2/Af | 50.0 °C | |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |