Impact strength of simply supported beam without notch
-30°C
ISO 179/1eU
55 kJ/m²
Impact strength of simply supported beam without notch
23°C
ISO 179/1eU
65 kJ/m²
Suspended wall beam without notch impact strength
-30°C
ISO 180/1U
55 kJ/m²
flammability
Test Condition
Test Method
Test Result
BurningBehavior
ISO 3795
passed
mechanical properties
Test Condition
Test Method
Test Result
tensile strength
Break,23°C
ISO 527-2/5
170 Mpa
elongation
Break,23°C
ASTM D638
3.2 %
tensile strength
Break,23°C
ASTM D638
165 Mpa
Tensile modulus
23°C
ISO 527-2/1
9400 Mpa
Tensile modulus
23°C
ASTM D638
8730 Mpa
Bending modulus
ASTM D790/ISO 178
9120 kg/cm²(MPa)[Lb/in²]
bending strength
ASTM D790/ISO 178
276 kg/cm²(MPa)[Lb/in²]
Tensile strain
Break,23°C
ISO 527-2/5
3.0 %
Bending modulus
23°C
ASTM D790
8000 Mpa
Bending modulus
23°C
ISO 178/A
8400 Mpa
bending strength
23°C
ASTM D790
260 Mpa
bending strength
3.5%Strain
ISO 178/A
255 Mpa
bending strength
23°C
ISO 178
260 Mpa
bending strength
FlexuralStrainatFlexuralStrength5(23°C)
3.6 %
Tensile modulus
ASTM D638/ISO 527
9910 kg/cm²(MPa)[Lb/in²]
tensile strength
ASTM D638/ISO 527
175 kg/cm²(MPa)[Lb/in²]
thermal performance
Test Condition
Test Method
Test Result
Linear coefficient of thermal expansion
TD：23to55°C
ISO 11359-2
1E-04 cm/cm/°C
Linear coefficient of thermal expansion
MD：23to55°C
ISO 11359-2
2E-05 cm/cm/°C
Melting temperature
ISO 11357-3
221 °C
Hot deformation temperature
0.45MPa,Unannealed
ISO 75-2/B
219 °C
Combustibility (rate)
UL 94
HB
Vicat softening temperature
ASTM D1525/ISO R306
210 ℃（℉）
Ball Pressure Test
210°C
IEC 60695-10-2
Pass
Vicat softening temperature
ISO 306/B120
210 °C
Hot deformation temperature
8.0MPa,Unannealed
ISO 75-2/C
150 °C
Hot deformation temperature
1.8MPa,Unannealed
ISO 75-2/A
210 °C
Physical properties
Test Condition
Test Method
Test Result
Water absorption rate
Equilibrium,23°C,50%RH
ISO 62
2.1 %
Water absorption rate
Saturation,23°C
ISO 62
7.0 %
Shrinkage rate
MD:120°C,2hr,2.00mm3
ISO 294-4
0.050 %
Shrinkage rate
MD:280°C,2.00mm2
ISO 294-4
0.29 %
Shrinkage rate
TD:120°C,2hr,2.00mm3
ISO 294-4
0.10 %
Shrinkage rate
TD:280°C,2.00mm2
ISO 294-4
0.81 %
Apparent density
ISO 60
0.60 g/cm³
density
ASTM D792/ISO 1183
1.36
Electrical performance
Test Condition
Test Method
Test Result
Compared to the anti leakage trace index
SolutionA
IEC 60112
PLC 1
Dielectric strength
23°C,1.00mm
IEC 60243-1
33 KV/mm
hardness
Test Condition
Test Method
Test Result
Ball Pressure Test
ISO 2039-1
193 Mpa
film
Test Condition
Test Method
Test Result
Thin film puncture strength
--6
ISO 6603-2
2.10 J
Thin film puncture strength
--7
ISO 6603-2
2.20 J
Thin film puncture strength
--6
ISO 6603-2
744 N
Thin film puncture strength
--7
ISO 6603-2
803 N
Supplementary Information
Test Condition
Test Method
Test Result
ISO Shortcut
ISO 1874
PA6.GHR.10-090.GF30
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)