Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates

PA6 BKV30GH2.0 900051 LANXESS GERMANY
Durethan®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | LANXESS GERMANY/BKV30GH2.0 900051 |
---|---|---|---|
Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 55 kJ/m² |
23°C | ISO 180/1U | 60 kJ/m² | |
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 65 kJ/m² |
-30°C | ISO 179/1eU | 55 kJ/m² |
Supplementary Information | Test Condition | Test Method | LANXESS GERMANY/BKV30GH2.0 900051 |
---|---|---|---|
ISO Shortcut | ISO 1874 | PA6.GHR.10-090.GF30 |
hardness | Test Condition | Test Method | LANXESS GERMANY/BKV30GH2.0 900051 |
---|---|---|---|
ball-indentation hardness | ISO 2039-1 | 193 Mpa |
film | Test Condition | Test Method | LANXESS GERMANY/BKV30GH2.0 900051 |
---|---|---|---|
Thin film puncture strength | --7 | ISO 6603-2 | 2.20 J |
--6 | ISO 6603-2 | 744 N | |
--7 | ISO 6603-2 | 803 N | |
--6 | ISO 6603-2 | 2.10 J |
Electrical performance | Test Condition | Test Method | LANXESS GERMANY/BKV30GH2.0 900051 |
---|---|---|---|
dielectric strength | 23°C,1.00mm | IEC 60243-1 | 33 KV/mm |
Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 1 |
Mechanical properties | Test Condition | Test Method | LANXESS GERMANY/BKV30GH2.0 900051 |
---|---|---|---|
bending strength | ASTM D790/ISO 178 | 276 kg/cm²(MPa)[Lb/in²] | |
Tensile strain | 断裂,23°C | ISO 527-2/5 | 3.0 % |
Flexural modulus | 23°C | ISO 178/A | 8400 Mpa |
bending strength | 3.5%Strain | ISO 178/A | 255 Mpa |
tensile strength | 断裂,23°C | ISO 527-2/5 | 170 Mpa |
Flexural modulus | ASTM D790/ISO 178 | 9120 kg/cm²(MPa)[Lb/in²] | |
bending strength | 23°C | ASTM D790 | 260 Mpa |
Tensile modulus | 23°C | ASTM D638 | 8730 Mpa |
23°C | ISO 527-2/1 | 9400 Mpa | |
tensile strength | 断裂,23°C | ASTM D638 | 165 Mpa |
ASTM D638/ISO 527 | 175 kg/cm²(MPa)[Lb/in²] | ||
bending strength | 23°C | ISO 178 | 260 Mpa |
Tensile modulus | ASTM D638/ISO 527 | 9910 kg/cm²(MPa)[Lb/in²] | |
Flexural modulus | 23°C | ASTM D790 | 8000 Mpa |
elongation | 断裂,23°C | ASTM D638 | 3.2 % |
bending strength | FlexuralStrainatFlexuralStrength5(23°C) | 3.6 % |
other | Test Condition | Test Method | LANXESS GERMANY/BKV30GH2.0 900051 |
---|---|---|---|
characteristic | 耐气候影响性能良好 热稳定性 |
Physical properties | Test Condition | Test Method | LANXESS GERMANY/BKV30GH2.0 900051 |
---|---|---|---|
density | ASTM D792/ISO 1183 | 1.36 |
flammability | Test Condition | Test Method | LANXESS GERMANY/BKV30GH2.0 900051 |
---|---|---|---|
Burning Behavior | ISO 3795 | passed |
physical property | Test Condition | Test Method | LANXESS GERMANY/BKV30GH2.0 900051 |
---|---|---|---|
Shrinkage rate | TD:120°C,2hr,2.00mm3 | ISO 294-4 | 0.10 % |
Apparent density | ISO 60 | 0.60 g/cm³ | |
Shrinkage rate | TD:280°C,2.00mm2 | ISO 294-4 | 0.81 % |
Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 2.1 % |
饱和,23°C | ISO 62 | 7.0 % | |
Shrinkage rate | MD:280°C,2.00mm2 | ISO 294-4 | 0.29 % |
MD:120°C,2hr,2.00mm3 | ISO 294-4 | 0.050 % |
Thermal performance | Test Condition | Test Method | LANXESS GERMANY/BKV30GH2.0 900051 |
---|---|---|---|
melting temperature | ISO 11357-3 | 221 °C | |
Combustibility (rate) | UL 94 | HB | |
vicat | ISO 306/B120 | 210 °C | |
ball-indentation hardness | 210°C | IEC 60695-10-2 | Pass |
Linear coefficient of thermal expansion | MD:23到55°C | ISO 11359-2 | 2E-05 cm/cm/°C |
vicat | ASTM D1525/ISO R306 | 210 ℃(℉) | |
Heat distortion temperature | 0.45MPa,未退火,HDT | ISO 75-2/B | 219 °C |
Linear coefficient of thermal expansion | TD:23to55°C | ISO 11359-2 | 1E-04 cm/cm/°C |
Heat distortion temperature | 1.8MPa,未退火,HDT | ISO 75-2/A | 210 °C |
8.0MPa,未退火,HDT | ISO 75-2/C | 150 °C |