impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	3.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	4.0	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Flammability level		UL 94	V-0
Flammability level	Flammability level		UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2	3400	Mpa
tensile strength	Yield	ISO 527-2	80.0	Mpa
Nominal tensile fracture strain		ISO 527-2	7.0	%
Bending modulus		ISO 178	3200	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	190	°C
Melting temperature		ISO 11357-3	295	°C
Linear coefficient of thermal expansion	Flow	ISO 11359-2	8.0E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	9.0E-5	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183	1.43	g/cm³
Shrinkage rate	横向Flow	ISO 294-4	1.5	%
Shrinkage rate	Shrinkage rate	Flow	ISO 294-4	1.5	%
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	2.4	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		IEC 60093	1.0E+15	ohms·cm
Dielectric strength		IEC 60243-1	30	KV/mm
Relative permittivity	100 Hz	IEC 60250	3.80
Relative permittivity	Relative permittivity	1 MHz	IEC 60250	3.50

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.