PA66 Ultramid® A3X2G7 BASF GERMANY
348
- Unit Price:US$ 6,006 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:59MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Electrical performance｜Flame retardant｜high strength｜High rigidity｜Oil resistant
- Application Areas:Electrical applications｜Electrical components
- Color:--
- Grade:Flame retardant grade
Material Certification
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | HDT | ASTM D648/ISO 75 | 250 ℃（℉） |
| melting temperature | 220 ℃（℉） | ||
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 1.5-2/6-7 mm/mm.℃ | |
| MD | 1.7E-05 cm/cm/°C | ||
| TD | 6.5E-05 cm/cm/°C | ||
| RTI Elec | 0.40mm | UL 746 | 110 °C |
| 0.75mm | UL 746 | 115 °C | |
| 1.5mm | UL 746 | 115 °C | |
| 3.0mm | UL 746 | 115 °C | |
| RTI Imp | 0.40mm | UL 746 | 115 °C |
| 0.75mm | UL 746 | 115 °C | |
| 1.5mm | UL 746 | 115 °C | |
| 3.0mm | UL 746 | 115 °C | |
| RTI Str | 0.75mm | UL 746 | 130 °C |
| 1.5mm | UL 746 | 130 °C | |
| 3.0mm | UL 746 | 130 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-0 |
| 1.5mm | UL 94 | V-0 | |
| 3.0mm | UL 94 | V-0 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179 | 65 kJ/m² |
| 23°C | ISO 179 | 70 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | ASTM D257/IEC 60093 | >1013/1010 Ω | |
| dielectric constant | ASTM D150/IEC 60250 | 3.6/5 | |
| volume resistivity | ASTM D257/IEC 60093 | 1015/1012 Ω.cm |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt volume flow rate | 275°C/5.0kg | ISO 1133 | 25.0 cm3/10min |
| shrinkage rate | TD | ISO 294-4 | 1.1 % |
| MD | ISO 294-4 | 0.34 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 14/18 kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 70/70 kg·cm/cm(J/M)ft·lb/in | ||
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 13/20 kg·cm/cm(J/M)ft·lb/in | |
| Elongation at break | ASTM D638/ISO 527 | 160/120 % | |
| Tensile modulus | ASTM D638/ISO 527 | 9200 kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ASTM D638/ISO 527 | 160/120 kg/cm²(MPa)[Lb/in²] | |
| elongation | ASTM D638/ISO 527 | 3/4 % | |
| Elongation at break | ASTM D638/ISO 527 | 3/4 % | |
| Tensile modulus | 23°C | ISO 527-2 | 11000 Mpa |
| tensile strength | 断裂,23°C | ISO 527-2 | 160 Mpa |
| Tensile strain | 断裂,23°C | ISO 527-2 | 3.0 % |
| flexural modulus | 23°C | ISO 178 | 9200 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.