Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 A3X2G7 BASF GERMANY
Ultramid®
Electrical applications,Electrical components
Electrical performance,Flame retardant,high strength,High rigidity,Oil resistant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF GERMANY/A3X2G7 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179 | 65 kJ/m² |
| 23°C | ISO 179 | 70 kJ/m² |
| Electrical performance | Test Condition | Test Method | BASF GERMANY/A3X2G7 |
|---|---|---|---|
| Surface Resistivity | ASTM D257/IEC 60093 | >1013/1010 Ω | |
| dielectric constant | ASTM D150/IEC 60250 | 3.6/5 | |
| Volume resistivity | ASTM D257/IEC 60093 | 1015/1012 Ω.cm |
| Mechanical properties | Test Condition | Test Method | BASF GERMANY/A3X2G7 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 13/20 kg·cm/cm(J/M)ft·lb/in | |
| Tensile strain | 断裂,23°C | ISO 527-2 | 3.0 % |
| elongation | ASTM D638/ISO 527 | 3/4 % | |
| Flexural modulus | 23°C | ISO 178 | 9200 Mpa |
| Tensile modulus | ASTM D638/ISO 527 | 9200 kg/cm²(MPa)[Lb/in²] | |
| 23°C | ISO 527-2 | 11000 Mpa | |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 70/70 kg·cm/cm(J/M)ft·lb/in | |
| tensile strength | 断裂,23°C | ISO 527-2 | 160 Mpa |
| elongation at break | ASTM D638/ISO 527 | 3/4 % | |
| tensile strength | ASTM D638/ISO 527 | 160/120 kg/cm²(MPa)[Lb/in²] |
| flammability | Test Condition | Test Method | BASF GERMANY/A3X2G7 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-0 |
| 3.0mm | UL 94 | V-0 | |
| 1.5mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | BASF GERMANY/A3X2G7 |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 1.1 % |
| MD | ISO 294-4 | 0.34 % | |
| Melt volume flow rate | 275°C/5.0kg | ISO 1133 | 25.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | BASF GERMANY/A3X2G7 |
|---|---|---|---|
| RTI Str | 0.75mm | UL 746 | 130 °C |
| RTI Imp | 1.5mm | UL 746 | 115 °C |
| RTI Elec | 0.40mm | UL 746 | 110 °C |
| 3.0mm | UL 746 | 115 °C | |
| RTI Imp | 3.0mm | UL 746 | 115 °C |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 1.5-2/6-7 mm/mm.℃ | |
| RTI Elec | 0.75mm | UL 746 | 115 °C |
| RTI Imp | 0.40mm | UL 746 | 115 °C |
| 0.75mm | UL 746 | 115 °C | |
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 250 ℃（℉） |
| Linear coefficient of thermal expansion | MD | 1.7E-05 cm/cm/°C | |
| RTI Str | 1.5mm | UL 746 | 130 °C |
| 3.0mm | UL 746 | 130 °C | |
| RTI Elec | 1.5mm | UL 746 | 115 °C |
| melting temperature | 220 ℃（℉） | ||
| Linear coefficient of thermal expansion | TD | 6.5E-05 cm/cm/°C |