PC PANLITE® AD-5503 TEIJIN JAPAN

540

Unit Price:US$ 5,450 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
99.8MT
Delivery Terms:
FOB
Port of Loading :
Shenzhen Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:transparent｜High mobility
Application Areas:Optical level
Color:--
Grade:Injection grade

Material Certification

SGS

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
Transmittance rate		ASTM D1003/ISO 13468	89	%
Refractive index		ASTM D542/ISO 489	1.585
transmissivity	3000μm	ASTM D1003	89.0	%
Refractive index		ASTM D542	1.585
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch		ISO 179	NoBreak
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	放置在23℃水中24h	ISO 62	0.2	%
Melt Volume Flow Rate (MVR)	300℃负荷1.2kg	ISO 1133	54	CM
Shrinkage rate	Flow	本公司制订的测定法	0.5-0.7	%
Refractive index		ASTM D542	1.585
Transmittance rate	试样厚度3mm	ASTM D1003	89	%
Shrinkage rate	Across Flow	本公司制订的测定法	0.5-0.7	%
density		ISO 1183	1200	kg/m
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ASTM D638/ISO 527	/2450	kg/cm²(MPa)[Lb/in²]
tensile strength		ASTM D638/ISO 527	/63	kg/cm²(MPa)[Lb/in²]
elongation		ASTM D638/ISO 527	/6	%
Bending modulus		ASTM D790/ISO 178	/2400	kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	/96	kg/cm²(MPa)[Lb/in²]
elongation at yield	50mm/min	ISO 527-1 and ISO 527-2	6	%
Impact strength of cantilever beam gap	没Notched	ISO 179	NB	KJ/m
Tensile stress	50mm/min	ISO 527-1 and ISO 527-2	63	Mpa
Bending modulus	2mm/min	ISO 178	2400	Mpa
bending strength	2mm/min	ISO 178	96	Mpa
Elongation at Break	50mm/min	ISO 527-1 and ISO 527-2	>50	%
Impact strength of cantilever beam gap	带Notched	ISO 179	3	KJ/m
Tensile modulus	1mm/min	ISO 527-1 and ISO 527-2	2450	Mpa
bending strength		ISO 178	96.0	Mpa
Bending modulus		ISO 178	2400	Mpa
Tensile strain	Break	ISO 527-2/50	>50	%
Tensile strain	Tensile strain	Yield	ISO 527-2/50	6.0	%
tensile strength	Yield	ISO 527-2/50	63.0	Mpa
Tensile modulus		ISO 527-2/1	2450	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature		ASTM D1525/ISO R306	143	℃（℉）
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	0.7	mm/mm.℃
Vicat softening temperature	50℃/h 50N	ISO 308	143	°C
Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	0.7	X10
Hot deformation temperature	1.80MPa	ISO 75-1 and ISO 75-2	124	°C
Linear coefficient of thermal expansion	Flow	ISO 11359-2	0.7	X10
Hot deformation temperature	0.45MPa	ISO 75-1 and ISO 75-2	138	°C
Linear coefficient of thermal expansion	TD	ISO 11359-2	7E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	ISO 11359-2	7E-05	cm/cm/°C
Vicat softening temperature		ISO 306/B50	143	°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	124	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	138	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792/ISO 1183	/1200
Shrinkage rate		ASTM D955	0.5-0.7	%
Water absorption rate		ASTM D570/ISO 62	0.2	%
Water absorption rate	Water absorption rate	23°C,24hr	ISO 62	0.20	%
Shrinkage rate	MD:4.00mm	Internal Method	0.50-0.70	%
Shrinkage rate	Shrinkage rate	TD:4.00mm	Internal Method	0.50-0.70	%
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	54.0	cm3/10min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric constant		ASTM D150/IEC 60250	3.1
	Dielectric constant		ASTM D150/IEC 60250	3
		Dielectric constant	100Hz	IEO 60250	3.1
		Dielectric constant	Dielectric constant	1MHz	IEO 60250	3
Volume resistivity		IEO 60250	>1×10	Ω.cm
Dielectric strength	短时间法	IEO 60243-1	30	MV/m
Dielectric loss	1MHz，Tangent	IEO 60250	90	X10
Arc resistance		IEO 60112	250
Dielectric loss	100Hz，Tangent	IEO 60250	10	X10
Surface resistivity		IEO 60250	>1×10	Ω
Dielectric strength		IEC 60243-1	30	KV/mm
Relative permittivity	100Hz	IEC 60250	3.10
Relative permittivity	Relative permittivity	1MHz	IEC 60250	3.00
Dissipation factor	100Hz	IEC 60250	1E-03
Volume resistivity		IEC 60093	>1.0E+15	ohms·cm
Surface resistivity		IEC 60093	>1.0E+15	ohms
Compared to the anti leakage trace index		IEC 60112	PLC 2
Dissipation factor	1MHz	IEC 60250	9E-03

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
Xiamen Aisuode	US$ 5390 /MT
Dongguan Juheng	US$ 5450 /MT
Dongguan Jianke	US$ 5450 /MT
Dongguan Sharp Plastic	US$ 5450 /MT
Dongguan Huateng Plastic	US$ 5450 /MT

Supplier Join

Get App

Top