Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC AD-5503 TEIJIN JAPAN
PANLITE®
Optical level
transparent,High mobility
SGS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodTEIJIN JAPAN/AD-5503
Impact strength of simply supported beam without notchISO 179NoBreak
Basic performanceTest ConditionTest MethodTEIJIN JAPAN/AD-5503
refractive indexASTM D5421.585
transmittance试样厚度3mmASTM D100389 %
Water absorption rate放置在23℃水中24hISO 620.2 %
Melt volume flow rate300℃负荷1.2kgISO 113354 CM
Shrinkage rate垂直方向本公司制订的测定法0.5-0.7 %
平行方向本公司制订的测定法0.5-0.7 %
densityISO 11831200 kg/m
Electrical performanceTest ConditionTest MethodTEIJIN JAPAN/AD-5503
Compared to the Leakage Tracking Index (CTI)IEC 60112PLC 2
dielectric constant100HzIEO 602503.1
ASTM D150/IEC 602503
Dielectric loss1MHz，正切IEO 6025090 X10
relative permittivity100HzIEC 602503.10
Dissipation Factor100HzIEC 602501E-03
dielectric constant1MHzIEO 602503
relative permittivity1MHzIEC 602503.00
arc resistanceIEO 60112250
Surface ResistivityIEO 60250>1×10 Ω
Dissipation Factor1MHzIEC 602509E-03
Dielectric loss100Hz，正切IEO 6025010 X10
dielectric strengthIEC 60243-130 KV/mm
短时间法IEO 60243-130 MV/m
Volume resistivityIEC 60093>1.0E+15 ohms·cm
IEO 60250>1×10 Ω.cm
Surface ResistivityIEC 60093>1.0E+15 ohms
Mechanical propertiesTest ConditionTest MethodTEIJIN JAPAN/AD-5503
bending strengthASTM D790/ISO 178/96 kg/cm²(MPa)[Lb/in²]
Tensile modulusISO 527-2/12450 Mpa
Flexural modulusASTM D790/ISO 178/2400 kg/cm²(MPa)[Lb/in²]
elongationASTM D638/ISO 527/6 %
Tensile modulus1mm/minISO 527-1 and ISO 527-22450 Mpa
elongation at yield50mm/minISO 527-1 and ISO 527-26 %
tensile strength ASTM D638/ISO 527/63 kg/cm²(MPa)[Lb/in²]
Tensile strain屈服ISO 527-2/506.0 %
Impact strength of cantilever beam gap带缺口ISO 1793 KJ/m
elongation at break50mm/minISO 527-1 and ISO 527-2>50 %
tensile strength 屈服ISO 527-2/5063.0 Mpa
Tensile stress50mm/minISO 527-1 and ISO 527-263 Mpa
bending strengthISO 17896.0 Mpa
Flexural modulusISO 1782400 Mpa
Tensile modulusASTM D638/ISO 527/2450 kg/cm²(MPa)[Lb/in²]
Impact strength of cantilever beam gap没缺口ISO 179NB KJ/m
Tensile strain断裂ISO 527-2/50>50 %
bending strength2mm/minISO 17896 Mpa
Flexural modulus2mm/minISO 1782400 Mpa
optical performance Test ConditionTest MethodTEIJIN JAPAN/AD-5503
transmissivity3000µmASTM D100389.0 %
refractive indexASTM D542/ISO 4891.585
ASTM D5421.585
transmittanceASTM D1003/ISO 1346889 %
Physical propertiesTest ConditionTest MethodTEIJIN JAPAN/AD-5503
Shrinkage rateASTM D9550.5-0.7 %
densityASTM D792/ISO 1183/1200
Water absorption rateASTM D570/ISO 620.2 %
physical property Test ConditionTest MethodTEIJIN JAPAN/AD-5503
Water absorption rate23°C,24hrISO 620.20 %
Melt volume flow rate300°C/1.2kgISO 113354.0 cm3/10min
Shrinkage rateMD:4.00mm内部方法0.50-0.70 %
TD:4.00mm内部方法0.50-0.70 %
Thermal performanceTest ConditionTest MethodTEIJIN JAPAN/AD-5503
vicatASTM D1525/ISO R306143 ℃（℉）
50℃/h 50NISO 308143 °C
Heat distortion temperature0.45MPa,未退火，HDTISO 75-2/B138 °C
1.80MPa，HDTISO 75-1 and ISO 75-2124 °C
vicatISO 306/B50143 °C
Heat distortion temperature1.8MPa,未退火，HDTISO 75-2/A124 °C
Linear coefficient of thermal expansion平行方向ISO 11359-20.7 X10
MDISO 11359-27E-05 cm/cm/°C
Heat distortion temperature0.45MPa，HDTISO 75-1 and ISO 75-2138 °C
Linear coefficient of thermal expansion垂直方向ISO 11359-20.7 X10
TDISO 11359-27E-05 cm/cm/°C
ASTM D696/ISO 113590.7 mm/mm.℃