Material Description
- Material Properties:High rigidity｜high strength｜Filler: Glass fiber reinforced material｜30% filler by weight
- Application Areas:Home appliance components｜Automotive Applications
- Color:--
- Grade:--
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 1.8MPa, Unanealed, 6.40mm | ASTM D648 | 175 °C | |
| 1.8MPa, Unanealed, 64.0mm span | ISO 75-2/Af | 158 °C | |
| Flow: -40 to 40 ° C | ASTME831 | 2.1E-05 cm/cm/°C | |
| Flow: 23 to 80 ° C | 23到80℃ | ASTME831 | 1.5E-05 cm/cm/°C |
| Flow: -40 to 40 ° C | ISO 11359-2 | 2.2E-05 cm/cm/°C | |
| Flow: 23 to 80 ° C | 23到80℃ | ISO 11359-2 | 1.6E-05 cm/cm/°C |
| Horizontal: -40 to 40 ° C | 横向, -40到40℃ | ASTME831 | 7.9E-05 cm/cm/°C |
| Horizontal: 23 to 80 ° C | 横向, 23到80℃ | ASTME831 | 4.5E-05 cm/cm/°C |
| Horizontal: -40 to 40 ° C | 横向, -40到40℃ | ISO 11359-2 | 8.2E-05 cm/cm/°C |
| Horizontal: 23 to 80 ° C | 横向, 23到80℃ | ISO 11359-2 | 1E-04 cm/cm/°C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/2U | 62 kJ/m² |
| -30°C | ASTM D256 | 120 J/m | |
| 23°C | ASTM D256 | 170 J/m | |
| -30°C | ISO 180/1A | 11 kJ/m² | |
| 23°C | ISO 180/1A | 14 kJ/m² | |
| ASTM D4812 | 840 J/m | ||
| ISO 180/1U | 52 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt volume flow rate | 250°C/5.0kg | ISO 1133 | 14.0 cm3/10min |
| 275°C/5.0kg | ISO 1133 | 26.0 cm3/10min | |
| shrinkage rate | MD | 内部方法 | 0.12 % |
| TD | 内部方法 | 0.28 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| volume resistivity | ASTM D257 | 1.1E+15 ohms·cm | |
| dielectric constant | 1.10GHz | 内部方法 | 3.53 |
| 1.90GHz | 内部方法 | 3.54 | |
| Dissipation Factor | 1.10GHz | 内部方法 | 0.012 |
| 1.90GHz | 内部方法 | 0.011 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| fracture | ASTM D638 | 110 Mpa | |
| ISO 527-2/5 | 120 Mpa | ||
| yield | ASTM D638 | 2.7 % | |
| ISO 527-2/5 | 2.5 % | ||
| fracture | ASTM D638 | 2.7 % | |
| ISO 527-2/5 | 2.5 % | ||
| 50.0mm span | ASTM D790 | 6600 Mpa | |
| --7 | ISO 178 | 7400 Mpa | |
| --8 | ISO 178 | 166 Mpa | |
| Fracture, 50.0mm span | ASTM D790 | 156 Mpa | |
| --1 | ASTM D638 | 7900 Mpa | |
| yield | ASTM D638 | 110 Mpa | |
| ISO 527-2/5 | 120 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.