PBT WF006N-BK1066 SABIC INNOVATIVE NANSHA

VALOX™

Home appliance components,Automotive Applications

High rigidity,high strength,Filler: Glass fiber reinf,30% filler by weight

--

--

--

--

--

--

--

--

--

--

--

--

--

--

--

Plastic Datasheets

thermal performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/WF006N-BK1066
1.8MPa, unannealed, 6.40mm		ASTM D648	175 °C
1.8MPa, unannealed, 64.0mm span of		ISO 75-2/Af	158 °C
Flow: 23 to 80 ° C	23to80℃	ISO 11359-2	1.6E-05 cm/cm/°C
Flow: 23 to 80 ° C		23to80℃	ASTME831	1.5E-05 cm/cm/°C
Flow: -40 to 40 ° C		ASTME831	2.1E-05 cm/cm/°C
Flow: -40 to 40 ° C			ISO 11359-2	2.2E-05 cm/cm/°C
Horizontal: 23 to 80 ° C	Across Flow, 23to80℃	ASTME831	4.5E-05 cm/cm/°C
Horizontal: 23 to 80 ° C		Across Flow, 23to80℃	ISO 11359-2	1E-04 cm/cm/°C
Horizontal: -40 to 40 ° C	Across Flow, -40to40℃	ASTME831	7.9E-05 cm/cm/°C
Horizontal: -40 to 40 ° C		Across Flow, -40to40℃	ISO 11359-2	8.2E-05 cm/cm/°C

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/WF006N-BK1066
--1		ASTM D638	7900 Mpa
50.0mm span		ASTM D790	6600 Mpa
--7		ISO 178	7400 Mpa
--8		ISO 178	166 Mpa
crack		ASTM D638	110 Mpa
			ISO 527-2/5	120 Mpa
			ASTM D638	2.7 %
			ISO 527-2/5	2.5 %
Fracture, 50.0mm span		ASTM D790	156 Mpa
yield		ASTM D638	2.7 %
			ISO 527-2/5	2.5 %
			ASTM D638	110 Mpa
			ISO 527-2/5	120 Mpa

Electrical performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/WF006N-BK1066
Dielectric constant	1.10GHz	Internal Method	3.53
Dielectric constant		1.90GHz	Internal Method	3.54
Dissipation factor	1.90GHz	Internal Method	0.011
Dissipation factor		1.10GHz	Internal Method	0.012
Volume resistivity		ASTM D257	1.1E+15 ohms·cm

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/WF006N-BK1066
Melt Volume Flow Rate (MVR)	275°C/5.0kg	ISO 1133	26.0 cm3/10min
Melt Volume Flow Rate (MVR)		250°C/5.0kg	ISO 1133	14.0 cm3/10min
Shrinkage rate	MD	Internal Method	0.12 %
Shrinkage rate		TD	Internal Method	0.28 %

impact performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/WF006N-BK1066
23°C		ASTM D256	170 J/m
			ASTM D4812	840 J/m
			ISO 180/1U	52 kJ/m²
			ISO 180/1A	14 kJ/m²
-30°C		ASTM D256	120 J/m
-30°C			ISO 180/1A	11 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/2U	62 kJ/m²