Material Description

Material Properties:Middle flow｜Biocompatibility｜Steam sterilization
Application Areas:Medical devices｜Medical and nursing supplies
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Reverse notch impact	3.20 mm	ASTM D256	1200	J/m
Dart impact	23°C, Total Energy	ASTM D3763	33.0	J
Dart impact	Dart impact	23°C	ASTM D3029	33.0	J
Suspended wall beam without notch impact strength	23°C	ASTM D4812	1300	J/m
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.71 mm	UL 94	V-2
	UL flame retardant rating	0.75 mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	3.0 mm	UL 94	5VA
Extreme Oxygen Index		ASTM D2863	44	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Taber abraser	1000 Cycles, 1000 g, CS-17 Wheel	ASTM D1044	10.0	mg
bending strength	Yield, 100 mm Span5	ASTM D790	165	Mpa
	bending strength	Yield, 50.0 mm Span4	ASTM D790	174	Mpa
	bending strength	bending strength	--6,7	ISO 178	160	Mpa
Bending modulus	--6	ISO 178	3300	Mpa
	Bending modulus	100 mm Span5	ASTM D790	3510	Mpa
	Bending modulus	Bending modulus	50.0 mm Span4	ASTM D790	3420	Mpa
elongation	Break	ISO 527-2/5	60	%
	elongation	Break3	ASTM D638	60	%
		elongation	Yield	ISO 527-2/5	6.0	%
		elongation	elongation	Yield3	ASTM D638	7.0	%
tensile strength	Break3	ASTM D638	105	Mpa
	tensile strength	Yield	ISO 527-2/5	105	Mpa
	tensile strength	tensile strength	Yield3	ASTM D638	110	Mpa
Tensile modulus	--	ISO 527-2/1	3200	Mpa
Tensile modulus	Tensile modulus	--2	ASTM D638	3580	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			150	°C
drying time			4.0 to 6.0	hr
Suggested maximum moisture content			0.020	%
Suggested injection volume			40 to 60	%
Temperature at the rear of the barrel			330 to 400	°C
Exhaust hole depth			0.025 to 0.076	mm
Temperature in the middle of the barrel			340 to 400	°C
Temperature at the front of the material cylinder			345 to 400	°C
Spray nozzle temperature			345 to 400	°C
Processing (melt) temperature			350 to 400	°C
Mold temperature			135 to 165	°C
Back pressure			0.300 to 0.700	Mpa
Screw speed			40 to 70	rpm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	207	°C
	Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	198	°C
	Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span9	ISO 75-2/Af	193	°C
Vicat softening temperature	--	ASTM D152510	218	°C
	Vicat softening temperature	--	ISO 306/B50	211	°C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	212	°C
Linear coefficient of thermal expansion	Flow : -20 to 150°C	ASTM E831	5.6E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Flow : -40 to 40°C	ISO 11359-2	5.0E-5	cm/cm/°C
		Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	5.0E-5	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	5.0E-5	cm/cm/°C
thermal conductivity		ASTM C177	0.22	W/m/K
RTI Elec		UL 746	170	°C
RTI Imp		UL 746	170	°C
RTI		UL 746	170	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.70	%
	Water absorption rate	Equilibrium, 23°C	ASTM D570	1.3	%
	Water absorption rate	Water absorption rate	Saturation, 23°C	ISO 62	1.3	%
Shrinkage rate	3.20 mm，Flow	Internal Method	0.50 - 0.70	%
Melt Volume Flow Rate (MVR)	360°C/5.0 kg	ISO 1133	25.0	cm3/10min
melt mass-flow rate	337°C/6.6 kg	ASTM D1238	18	g/10 min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		ASTM D257	1.0E+17	ohms·cm
Dielectric strength	1.60 mm, in Air	ASTM D149	33	KV/mm
Dielectric strength	Dielectric strength	1.60 mm, in Oil	ASTM D149	28	KV/mm
Dielectric constant	1 kHz	ASTM D150	3.15
Dissipation factor	1 kHz	ASTM D150	1.3E-3
Dissipation factor	Dissipation factor	2.45 GHz	ASTM D150	2.5E-3
Arc resistance		ASTM D495	PLC 5
Compared to the anti leakage trace index		UL 746	PLC 4
High arc combustion index		UL 746	PLC 3
High voltage arc tracing rate		UL 746	PLC 2
Hot wire ignition		UL 746	PLC 1
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	M-Scale	ASTM D785	109

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
Guangzhou HuShang Chemical	US$ 30390 /MT

Supplier Join

Get App

Top

PEI ULTEM™ HU1010-7HD395 SABIC INNOVATIVE US

Material Description

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index