PEI HU1010-7HD395 SABIC INNOVATIVE US
ULTEM™ 
Medical devices,Medical and nursing supplies
Middle flow,Biocompatibility,Steam sterilization
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

hardnessTest ConditionTest MethodSABIC INNOVATIVE US/HU1010-7HD395
Rockwell hardnessM-ScaleASTM D785109
thermal performanceTest ConditionTest MethodSABIC INNOVATIVE US/HU1010-7HD395
Hot deformation temperature1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span9ISO 75-2/Af193 °C
0.45 MPa, Unannealed, 6.40 mmASTM D648207 °C
1.8 MPa, Unannealed, 6.40 mmASTM D648198 °C
Linear coefficient of thermal expansionFlow : -20 to 150°CASTM E8315.6E-5 cm/cm/°C
Across Flow : -40°CISO 11359-25.0E-5 cm/cm/°C
Flow : -40 to 40°CISO 11359-25.0E-5 cm/cm/°C
Across Flow : -40 to 40°CASTM E8315.0E-5 cm/cm/°C
RTIUL 746170 °C
RTI ElecUL 746170 °C
RTI ImpUL 746170 °C
thermal conductivityASTM C1770.22 W/m/K
Vicat softening temperature--ISO 306/B120212 °C
--ISO 306/B50211 °C
--ASTM D152510218 °C
mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/HU1010-7HD395
Bending modulus--6ISO 1783300 Mpa
100 mm Span5ASTM D7903510 Mpa
50.0 mm Span4ASTM D7903420 Mpa
bending strengthYield, 50.0 mm Span4ASTM D790174 Mpa
--6,7ISO 178160 Mpa
Yield, 100 mm Span5ASTM D790165 Mpa
elongationBreakISO 527-2/560 %
Yield3ASTM D6387.0 %
YieldISO 527-2/56.0 %
Break3ASTM D63860 %
Taber abraser1000 Cycles, 1000 g, CS-17 WheelASTM D104410.0 mg
Tensile modulus--2ASTM D6383580 Mpa
--ISO 527-2/13200 Mpa
tensile strengthYieldISO 527-2/5105 Mpa
Break3ASTM D638105 Mpa
Yield3ASTM D638110 Mpa
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE US/HU1010-7HD395
Arc resistanceASTM D495PLC 5
Compared to the anti leakage trace indexUL 746PLC 4
Dielectric constant1 kHzASTM D1503.15
Dielectric strength1.60 mm, in AirASTM D14933 KV/mm
1.60 mm, in OilASTM D14928 KV/mm
Dissipation factor2.45 GHzASTM D1502.5E-3
1 kHzASTM D1501.3E-3
High arc combustion indexUL 746PLC 3
High voltage arc tracing rateUL 746PLC 2
Hot wire ignitionUL 746PLC 1
Volume resistivityASTM D2571.0E+17 ohms·cm
Physical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/HU1010-7HD395
melt mass-flow rate337°C/6.6 kgASTM D123818 g/10 min
Melt Volume Flow Rate (MVR)360°C/5.0 kgISO 113325.0 cm3/10min
Shrinkage rate3.20 mm，FlowInternal Method0.50 - 0.70 %
Water absorption rateEquilibrium, 23°CASTM D5701.3 %
Saturation, 23°CISO 621.3 %
Equilibrium, 23°C, 50% RHISO 620.70 %
impact performanceTest ConditionTest MethodSABIC INNOVATIVE US/HU1010-7HD395
Dart impact23°CASTM D302933.0 J
23°C, Total EnergyASTM D376333.0 J
Reverse notch impact3.20 mmASTM D2561200 J/m
Suspended wall beam without notch impact strength23°CASTM D48121300 J/m
flammabilityTest ConditionTest MethodSABIC INNOVATIVE US/HU1010-7HD395
Extreme Oxygen IndexASTM D286344 %
UL flame retardant rating0.71 mmUL 94V-2
3.0 mmUL 945VA
0.75 mmUL 94V-0
injectionTest ConditionTest MethodSABIC INNOVATIVE US/HU1010-7HD395
Back pressure0.300 to 0.700 Mpa
drying temperature150 °C
drying time4.0 to 6.0 hr
Exhaust hole depth0.025 to 0.076 mm
Mold temperature135 to 165 °C
Processing (melt) temperature350 to 400 °C
Screw speed40 to 70 rpm
Spray nozzle temperature345 to 400 °C
Suggested injection volume40 to 60 %
Suggested maximum moisture content0.020 %
Temperature at the front of the material cylinder345 to 400 °C
Temperature at the rear of the barrel330 to 400 °C
Temperature in the middle of the barrel340 to 400 °C