PC LEXAN™ DMX1435-GY6E563T SABIC INNOVATIVE SINGAPHORE
202
- Unit Price:US$ 9,637 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:38MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Scratch resistant｜High temperature resistance｜high strength
- Application Areas:Electronic and electrical components｜Automotive components｜Wire and cable
- Color:--
- Grade:--
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | 108 | |
| ASTM D785 | 93 | ||
| Hardness | ASTM D3363 | H | |
| ball-indentation hardness | ISO 2039 | 128 Mpa |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| transmissivity | ASTM DI 003 | 88 % | |
| Haze ratio | ASTM D1003 | 0.8 % | |
| refractive index | ASTM D542 | 1.584 | |
| ISO 489 | 1.584 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | ASTM D648 | 133 °C | |
| ASTM D648 | 119 °C | ||
| ISO 75 | 131 °C | ||
| ISO 75 | 118 °C | ||
| vicat | ASTM DI 525 | 139 °C | |
| ISO 306 | 138 °C | ||
| ISO 306 | 140 °C | ||
| Linear expansion coefficient flow | ASTM E831 | 0.000070 cm/cm/℃ | |
| Vertical expansion coefficient | ASTM E831 | 0.000070 cm/cm/℃ | |
| Linear coefficient of thermal expansion | ISO 11359 | 0.000070 cm/cm/℃ | |
| ISO 11359 | 0.000070 cm/cm/℃ | ||
| thermal conductivity | ASTM C177 | 0.2 w/(m.℃) | |
| ISO 8302 | 0.2 w/(m.℃) | ||
| specific heat | ASTM C351 | 1.4 J/(g.℃) | |
| Ball indentation test | IEC 60695 | 125 °C | |
| IEC 60695 | 140 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2900 Mpa | |
| ISO 527 | 2450 Mpa | ||
| tensile strength | ASTM D638 | 80 Mpa | |
| ASTM D638 | 65 Mpa | ||
| ISO 527 | 80 Mpa | ||
| ISO 527 | 60 Mpa | ||
| elongation | ASTM D638 | 7 % | |
| ASTM D638 | 70 % | ||
| ISO 527 | 7 % | ||
| ISO 527 | 40 % | ||
| bending strength | ASTM D790 | 120 Mpa | |
| ISO 178 | 108 Mpa | ||
| flexural modulus | ASTM D790 | 2600 Mpa | |
| ISO 178 | 2450 Mpa | ||
| Impact strength of cantilever beam gap | ASTM D256 | 30 J/m | |
| ASTM D256 | 30 J/m | ||
| ISO 180 | 5 kJ/m² | ||
| ISO 180 | 4 kJ/m² | ||
| Suspended wall beam without notch impact strength | ASTM D4812 | NB J/m | |
| ISO 180 | NB kJ/m² | ||
| Impact strength of cantilever beam gap | ISO 180 | 45 kJ/m² | |
| Charpy Notched Impact Strength | ISO 179 | 3 kJ/m² | |
| ISO 179 | 3 kJ/m² | ||
| ISO 179 | NB kJ/m² | ||
| ISO 179 | 47 kJ/m² | ||
| Taber wear resistance | ASTM D1044 | 10 mg/1000cy | |
| Taiberten loss | 内部测试方法 | 10 mg/1000cy | |
| Erichsen scratch depth | 内部测试方法 | 14 micrometer | |
| Instrumented impact | ASTM D3763 | 30 J |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792 | 1.2 g/cm³ | |
| ISO 1183 | 1.17 g/cm³ | ||
| shrinkage rate | 内部测试方法 | 0.5-0.8 % | |
| Water absorption rate | ASTM D570 | 0.08 % | |
| ASTM D570 | 0.28 % | ||
| ASTM D570 | 0.13 % | ||
| ASTM D570 | 0.04 % | ||
| ISO 62 | 0.27 % | ||
| ISO 62 | 0.13 % | ||
| melt mass-flow rate | ASTM D1238 | 14.5 g/10min | |
| ISO 1133 | 13 cm3/10min | ||
| specific volume | ASTM D792 | 0.85 cm³/g |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.