Material Comparison

Product Info

Product Name

Brand Name

Usages

Properties

Certificates

PC DMX1435-GY6E563T SABIC INNOVATIVE SINGAPHORE

LEXAN™

Electronic and electrical components,Automotive components,Wire and cable

Scratch resistant,High temperature resistan,high strength

Plastic Datasheets

hardness	Test Condition	Test Method	SABIC INNOVATIVE SINGAPHORE/DMX1435-GY6E563T
Ball Pressure Test	H358/30	ISO 2039	128 Mpa
Pencil hardness	1.0kg	ASTM D3363	H
Rockwell hardness	M标尺	ASTM D785	93
Rockwell hardness		L标尺	ASTM D785	108

thermal performance	Test Condition	Test Method	SABIC INNOVATIVE SINGAPHORE/DMX1435-GY6E563T
Ball indentation test		IEC 60695	140 °C
Hot deformation temperature	Unannealed1.8MPa 3.2mm	ASTM D648	119 °C
		0.45MPa 4.0mm	ISO 75	131 °C
		Unannealed0.45MPa 3.2mm	ASTM D648	133 °C
		1.8MPa 4.0mm	ISO 75	118 °C
Linear coefficient of thermal expansion	Flow23~80℃	ISO 11359	0.000070 cm/cm/℃
Linear coefficient of thermal expansion		垂直23~80℃	ISO 11359	0.000070 cm/cm/℃
Linear expansion coefficient flow	-40.0~95℃	ASTM E831	0.000070 cm/cm/℃
specific heat		ASTM C351	1.4 J/(g.℃)
thermal conductivity		ISO 8302	0.2 w/(m.℃)
thermal conductivity			ASTM C177	0.2 w/(m.℃)
Vertical expansion coefficient	-40.0~95℃	ASTM E831	0.000070 cm/cm/℃
Vicat softening temperature	50℃/hr 50N	ISO 306	138 °C
		120℃/hr 50N	ISO 306	140 °C
		50℃/hr 50N	ASTM DI 525	139 °C

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE SINGAPHORE/DMX1435-GY6E563T
Bending modulus	2.0mm/min	ISO 178	2450 Mpa
Bending modulus		1.3mm/min	ASTM D790	2600 Mpa
bending strength	Yield1.3mm/min	ASTM D790	120 Mpa
bending strength		Yield2.0mm/min	ISO 178	108 Mpa
Charpy Notched Impact Strength	23°C3.0mm 1eA型	ISO 179	3 kJ/m²
		30℃ 3.0mm 1eA型^	ISO 179	3 kJ/m²
		-30℃ 3.0mm	ISO 179	47 kJ/m²
		23°C 3.0mm	ISO 179	NB kJ/m²
elongation	Break50mm/min	ISO 527	40 %
		Yield50mm/min iI型	ASTM D638	7 %
		Yield50mm/min	ISO 527	7 %
		Break50mm/min I型	ASTM D638	70 %
Erichsen scratch depth	6N	内部测试方法	14 micrometer
Impact strength of cantilever beam gap	-30℃ 3.0mm	ISO 180	45 kJ/m²
		-30℃	ASTM D256	30 J/m
		23℃	ASTM D256	30 J/m
		“-30℃ 3.0mm A型Notched	ISO 180	4 kJ/m²
		23°C 3.0mm A型Notched	ISO 180	5 kJ/m²
Instrumented impact	23℃总能量	ASTM D3763	30 J
Suspended wall beam without notch impact strength	23°C 3.0mm	ISO 180	NB kJ/m²
Suspended wall beam without notch impact strength		23℃	ASTM D4812	NB J/m
Taber wear resistance	CS-17轮1kg	ASTM D1044	10 mg/1000cy
Taiberten loss	CS-17轮1kg	内部测试方法	10 mg/1000cy
Tensile modulus	1.0mm/min	ISO 527	2450 Mpa
Tensile modulus		50mm/min	ASTM D638	2900 Mpa
tensile strength	Break50mm/mini型	ASTM D638	65 Mpa
		Yield50mm/min	ISO 527	80 Mpa
		Yield50mm/min I型	ASTM D638	80 Mpa
		斯裂50mm/min	ISO 527	60 Mpa

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE SINGAPHORE/DMX1435-GY6E563T
Bi Rong		ASTM D792	0.85 cm³/g
density		ISO 1183	1.17 g/cm³
density			ASTM D792	1.2 g/cm³
melt mass-flow rate	300℃ 1.2kg	ISO 1133	13 cm3/10min
melt mass-flow rate		300℃ 1.2kg	ASTM D1238	14.5 g/10min
Shrinkage rate	Flow3.2mm	内部测试方法	0.5-0.8 %
Water absorption rate	23℃Equilibrium	ASTM D570	0.28 %
		50RH 24hr	ASTM D570	0.04 %
		23℃ 50RH	ISO 62	0.13 %
		50RHEquilibrium	ASTM D570	0.13 %
		24hr	ASTM D570	0.08 %
		23℃Saturation	ISO 62	0.27 %

optical performance	Test Condition	Test Method	SABIC INNOVATIVE SINGAPHORE/DMX1435-GY6E563T
Refractive index		ASTM D542	1.584
Refractive index			ISO 489	1.584
transmissivity	2540pm	ASTM DI 003	88 %
turbidity	2540Pm	ASTM D1003	0.8 %