ABS

ABS POLYLAC® PA-709 TAIWAN CHIMEI

497

Unit Price:US$ 2,019 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
399.5MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details
Material Comparison:
ABS TAIRILAC® AG12A0 FCFC TAIWAN

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High impact resistance｜Low temperature resistance
Application Areas:Automotive sector
Color:--
Grade:Injection grade

Material Certification

MSDS

RoHS

TDS

MSDS

RoHS

SVHC

Processing

Statement

REACH

Technical Data Sheet

other	Test Condition	Test Method	Test Result
purpose			水管配件 / 汽车前后扰流板 / 摩托车挡板 / 押出水管 / 安全帽
characteristic			超高耐冲击强度押管用。
remarks			在射出周期中勿将热融胶长期停留在加热管中

machinability	Test Condition	Test Method	Test Result
Dry conditions			80°C下烘料约2-3小时
Processing temperature			180-220 °C
	Processing temperature			190-230 °C
	Processing temperature	Processing temperature			180-230°C °C
Screw speed			- rpm
Mold temperature			30-70 °C
Melt Temperature			- °C
pressure			- Mpa

mechanical properties	Test Condition	Test Method	Test Result
Elongation at Break		ASTM D638/ISO 527	- %
Impact strength of cantilever beam gap		ASTM D256/ISO 179	45（8.4） kg·cm/cm(J/M)ft·lb/in
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ASTM D256/ISO 179	- kg·cm/cm(J/M)ft·lb/in
Charpy Notched Impact Strength		ASTM D256/ISO 179	- kg·cm/cm(J/M)ft·lb/in
bending strength		ASTM D790/ISO 178	640（9.070） kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	23000（32000） kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	R-102
elongation		ASTM D638/ISO 527	40 %
tensile strength		ASTM D638/ISO 527	400（5.670） kg/cm²(MPa)[Lb/in²]
Tensile modulus		ASTM D638/ISO 527	- kg/cm²(MPa)[Lb/in²]
Elongation at Break		ASTM D638/ISO 527	- %
Impact strength of cantilever beam gap		ASTM D256/ISO 179	37（6.9） kg·cm/cm(J/M)ft·lb/in

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	- mm/mm.℃
Vicat softening temperature		ASTM D1525/ISO R306	105（221） ℃（℉）
Hot deformation temperature	HDT	ASTM D648/ISO 75	88（190） ℃（℉）
Hot deformation temperature	Hot deformation temperature	HDT	ASTM D648/ISO 75	99（210） ℃（℉）
Combustibility (rate)		UL 94	1.6mmHB

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate		ASTM D1238/ISO 1133	5 g/10min
melt mass-flow rate	melt mass-flow rate		ASTM D1238/ISO 1133	0.5 g/10min
Water absorption rate		ASTM D570/ISO 62	- %
Shrinkage rate		ASTM D955	- %
density		ASTM D792/ISO 1183	1.03

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

ABS POLYLAC® PA-709 TAIWAN CHIMEI

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet