PPO/PA NORYL GTX™ GTX678-74709 SABIC INNOVATIVE US

353

Unit Price:US$ 4,075 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
65MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Hydrolysis resistance｜High temperature resistance｜Dimensional stability｜High mobility
Application Areas:Industrial machinery｜Electrical applications
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	23°C	ISO 179/1eA	12 kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	60.0 J

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5mm	UL 94	V-1
UL flame retardant rating	UL flame retardant rating	2.0mm	UL 94	V-05VB5VA
Burning wire flammability index	2.0mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	1.0mm	IEC 60695-2-13	800 °C

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	--3	ASTM D638	2900 Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2900 Mpa
tensile strength	Yield4	ASTM D638	58.0 Mpa
	tensile strength	Yield	ISO 527-2/50	58.0 Mpa
		tensile strength	Break4	ASTM D638	52.0 Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	52.0 Mpa
elongation	Yield4	ASTM D638	7.0 %
	elongation	Yield	ISO 527-2/50	7.0 %
		elongation	Break4	ASTM D638	12 %
		elongation	elongation	Break	ISO 527-2/50	12 %
Bending modulus	50.0mmSpan5	ASTM D790	2600 Mpa
Bending modulus	Bending modulus	--6	ISO 178	2600 Mpa
bending strength	--6,7	ISO 178	95.0 Mpa
bending strength	bending strength	Yield,50.0mmSpan5	ASTM D790	95.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	195 °C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,64.0mmSpan10	ISO 75-2/Bf	191 °C
Vicat softening temperature	--	ASTM D152511	198 °C
	Vicat softening temperature	--	ISO 306/B50	197 °C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	195 °C
Ball Pressure Test	125°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	MD:-40to40°C	ASTME831	7.8E-05 cm/cm/°C
	Linear coefficient of thermal expansion	MD:23to60°C	ISO 11359-2	8.3E-05 cm/cm/°C
		Linear coefficient of thermal expansion	TD:-40to40°C	ASTME831	8E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:23to60°C	ISO 11359-2	8.5E-05 cm/cm/°C
specific heat		ASTMC351	1400 J/kg/°C
thermal conductivity		ASTMC177	0.20 W/m/K

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	300°C/5.0kg	ASTM D1238	7.8 g/10min
Melt Volume Flow Rate (MVR)	300°C/5.0kg	ISO 1133	7.00 cm3/10min
Shrinkage rate	MD：3.20mm	Internal Method	1.3-1.5 %
Water absorption rate	Saturation,23°C	ISO 62	4.0 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.50 %

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		ASTM D257	4E+03 ohms·cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PPO/PA NORYL GTX™ GTX678-74709 SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet