PPO/PA GTX678-74709 SABIC INNOVATIVE US
NORYL GTX™
Industrial machinery、Electrical applications
Hydrolysis resistance、High temperature resistan、Dimensional stability、High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/GTX678-74709 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 12 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 60.0 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/GTX678-74709 |
|---|---|---|---|
| tensile strength | 屈服4 | ASTM D638 | 58.0 Mpa |
| elongation | 断裂4 | ASTM D638 | 12 % |
| bending strength | 屈服,50.0mm跨距5 | ASTM D790 | 95.0 Mpa |
| Tensile modulus | --3 | ASTM D638 | 2900 Mpa |
| elongation | 断裂 | ISO 527-2/50 | 12 % |
| Flexural modulus | 50.0mm跨距5 | ASTM D790 | 2600 Mpa |
| bending strength | --6,7 | ISO 178 | 95.0 Mpa |
| Flexural modulus | --6 | ISO 178 | 2600 Mpa |
| tensile strength | 断裂 | ISO 527-2/50 | 52.0 Mpa |
| 屈服 | ISO 527-2/50 | 58.0 Mpa | |
| elongation | 屈服 | ISO 527-2/50 | 7.0 % |
| 屈服4 | ASTM D638 | 7.0 % | |
| tensile strength | 断裂4 | ASTM D638 | 52.0 Mpa |
| Tensile modulus | -- | ISO 527-2/1 | 2900 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/GTX678-74709 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 4E+03 ohms·cm |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/GTX678-74709 |
|---|---|---|---|
| UL flame retardant rating | 2.0mm | UL 94 | V-05VB5VA |
| Hot filament ignition temperature | 1.0mm | IEC 60695-2-13 | 800 °C |
| UL flame retardant rating | 1.5mm | UL 94 | V-1 |
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 960 °C |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/GTX678-74709 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 1.3-1.5 % |
| Melt volume flow rate | 300°C/5.0kg | ISO 1133 | 7.00 cm3/10min |
| melt mass-flow rate | 300°C/5.0kg | ASTM D1238 | 7.8 g/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.50 % |
| 饱和,23°C | ISO 62 | 4.0 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/GTX678-74709 |
|---|---|---|---|
| vicat | -- | ASTM D152511 | 198 °C |
| -- | ISO 306/B120 | 195 °C | |
| Linear coefficient of thermal expansion | TD:23到60°C | ISO 11359-2 | 8.5E-05 cm/cm/°C |
| thermal conductivity | ASTMC177 | 0.20 W/m/K | |
| Linear coefficient of thermal expansion | MD:23到60°C | ISO 11359-2 | 8.3E-05 cm/cm/°C |
| TD:-40到40°C | ASTME831 | 8E-05 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 195 °C |
| vicat | -- | ISO 306/B50 | 197 °C |
| Heat distortion temperature | 0.45MPa,未退火,64.0mm跨距10，HDT | ISO 75-2/Bf | 191 °C |
| specific heat | ASTMC351 | 1400 J/kg/°C | |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | 通过 |
| Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 7.8E-05 cm/cm/°C |