Material Description
- Material Properties:enhance｜Glass fiber reinforced
- Application Areas:Electrical applications｜Home appliance components
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ISO 294-4 | 0.50 % | |
| ISO 294-4 | 0.20 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1A | 12000 Mpa | |
| tensile strength | ISO 527-2/1A/5 | 120 Mpa | |
| Tensile strain | ISO 527-2/1A/5 | 1.4 % | |
| Flexural modulus | ISO 178 | 12000 Mpa | |
| bending strength | ISO 178 | 185 Mpa | |
| Fracture bending strain | ISO 178 | 2.0 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179/1eU | 10 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 1.0E+11 ohms | |
| Volume resistivity | IEC 60093 | 1.0E+16 ohms·cm | |
| relative permittivity | IEC 60250 | 4.00 | |
| Dissipation Factor | IEC 60250 | 7.0E-3 | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 150 to 170 °C | ||
| drying time | 6.0 hr | ||
| Hopper temperature | 20 to 40 °C | ||
| Temperature at the rear of the barrel | 330 to 350 °C | ||
| Temperature in the middle of the barrel | 340 to 360 °C | ||
| Temperature at the front of the material cylinder | 345 to 365 °C | ||
| Spray nozzle temperature | 355 to 370 °C | ||
| Processing (melt) temperature | 360 to 375 °C | ||
| Temperature | 80 to 120 °C | ||
| injection speed | 中等 | ||
| Back pressure | < 3.00 Mpa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/A | 315 °C | |
| ISO 75-2/C | 271 °C | ||
| melting temperature | ISO 11357-3 | 350 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 8.0E-6 cm/cm/°C | |
| ISO 11359-2 | 1.7E-5 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.