ULDPE

ULDPE ATTANE™ 4203 STYRON US

368

Unit Price:US$ 2,135 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
23.5MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High impact resistance｜Low temperature resistance｜Compliant with Canadian HPFB certification｜Excellent elasticity and｜Resistance to cracking and sealing performance
Application Areas:film｜container｜chip｜Used for packaging
Color:--
Grade:Blow molding grade

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
transparency	20μm	ASTM D1746	93
gloss	20 μm	ASTM D2457	48
turbidity		ASTM D1003	5 %
gloss	45°	ASTM D2457	39
turbidity		ASTM D1003	14 %

Other performance	Test Condition	Test Method	Test Result
Starting temperature of heat sealing		陶氏企业测试	88 °C

Basic Performance	Test Condition	Test Method	Test Result
melt mass-flow rate		ASTM D1238	0.8 g/10min
density		ASTM D792	0.905

mechanical properties	Test Condition	Test Method	Test Result
Puncture intensity	(20 μm)	陶氏企业测试	22 J/cm
tensile strength	Yield	ASTM D882	9 Mpa
tensile strength	tensile strength	20 μm (MD)	ASTM D882	53 Mpa
Elongation at Break	20μm (MD)	ASTM D882	445 %

thermal performance	Test Condition	Test Method	Test Result
Vicat softening temperature		ASTM D1525	84 °C
Vicat softening temperature	Vicat softening temperature		ASTM D1525	83.9 °C
Melting temperature		Internal Method	123 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	190°C/2.16kg	ASTM D1238	0.80 g/10min

film	Test Condition	Test Method	Test Result
film thickness			25 µm
Thin film puncture strength		Internal Method	4.52 J
	Thin film puncture strength		Internal Method	48.9 N
	Thin film puncture strength	Thin film puncture strength		Internal Method	24.8 J/cm³
Membrane strength	MD	ASTM D882	45.5 J/cm³
Membrane strength	Membrane strength	TD	ASTM D882	64.5 J/cm³
Secant modulus	1%Secant,MD	ASTM D882	98.6 Mpa
	Secant modulus	2%Secant,MD	ASTM D882	89.6 Mpa
		Secant modulus	1%Secant,TD	ASTM D882	113 Mpa
		Secant modulus	Secant modulus	2%Secant,TD	ASTM D882	93.8 Mpa
tensile strength	MD:Yield	ASTM D882	6.21 Mpa
	tensile strength	TD:Yield	ASTM D882	5.86 Mpa
		tensile strength	MD:Break	ASTM D882	32.4 Mpa
		tensile strength	tensile strength	TD:Break	ASTM D882	30.0 Mpa
elongation	MD:Break	ASTM D882	340 %
elongation	elongation	TD:Break	ASTM D882	570 %
Dart impact		ASTM D1709B	>1100 g
Elmendorf tear strength	MD	ASTM D1922	370 g
Elmendorf tear strength	Elmendorf tear strength	TD	ASTM D1922	520 g

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

ULDPE ATTANE™ 4203 STYRON US

Material Description

Technical Data Sheet Compare

Technical Data Sheet