ULDPE 4203 STYRON US
ATTANE™
film、container、chip、Used for packaging
High impact resistance、Low temperature resistanc、Compliant with Canadian H、Excellent elasticity and、Resistance to cracking an
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Other performanceTest ConditionTest MethodSTYRON US/4203
Starting temperature of heat sealing陶氏企业测试88 °C
filmTest ConditionTest MethodSTYRON US/4203
film strengthMDASTM D88245.5 J/cm³
Secant modulus2%正割,TDASTM D88293.8 Mpa
Thin film puncture strength内部方法4.52 J
Secant modulus1%正割,TDASTM D882113 Mpa
tensile strength MD:屈服ASTM D8826.21 Mpa
elongationMD:断裂ASTM D882340 %
Thin film puncture strength内部方法24.8 J/cm³
内部方法48.9 N
tensile strength TD:屈服ASTM D8825.86 Mpa
Elmendorf tear strengthMDASTM D1922370 g
Dart impactASTM D1709B>1100 g
film thickness25 µm
tensile strength MD:断裂ASTM D88232.4 Mpa
TD:断裂ASTM D88230.0 Mpa
film strengthTDASTM D88264.5 J/cm³
Secant modulus2%正割,MDASTM D88289.6 Mpa
Elmendorf tear strengthTDASTM D1922520 g
Secant modulus1%正割,MDASTM D88298.6 Mpa
elongationTD:断裂ASTM D882570 %
Basic performanceTest ConditionTest MethodSTYRON US/4203
densityASTM D7920.905 g/cm
melt mass-flow rateASTM D12380.8 g/10min
Mechanical propertiesTest ConditionTest MethodSTYRON US/4203
tensile strength 20 μm (MD)ASTM D88253 Mpa
elongation at break20μm (MD)ASTM D882445 %
Puncture Strength(20 μm)陶氏企业测试22 J/cm
tensile strength 屈服ASTM D8829 Mpa
optical performance Test ConditionTest MethodSTYRON US/4203
gloss20 μmASTM D245748
45°ASTM D245739
transparency20μmASTM D174693
Haze ratioASTM D100314 %
physical property Test ConditionTest MethodSTYRON US/4203
melt mass-flow rate190°C/2.16kgASTM D12380.80 g/10min
Thermal performanceTest ConditionTest MethodSTYRON US/4203
vicatASTM D152583.9 °C
melting temperature内部方法123 °C