PA6 RADILON® S RV300 RADIC ITALY

273

Unit Price:US$ 3,148 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
40.5MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High rigidity｜Dimensional stability｜Glass fiber reinforced｜enhance
Application Areas:--
Color:--
Grade:Enhanced level

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	9.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	11 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	60 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	68 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.8 mm	UL 94	HB
Burning wire flammability index	2.0 mm	IEC 60695-2-12	700 °C
flammability	3.00 mm	FMVSS 302	0 mm/min

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2/1A/1	9600 Mpa
tensile strength	Break	ISO 527-2/1A/5	175 Mpa
Tensile strain	Break	ISO 527-2/1A/5	3.1 %
Bending modulus		ISO 178	8550 Mpa
bending strength		ISO 178	245 Mpa

injection	Test Condition	Test Method	Test Result
Drying temperature - hot air dryer			80 °C
Drying time - hot air dryer			2.0 to 4.0 hr
Dew Point - Hot Air Drying Machine			-20 °C
Suggested maximum moisture content			0.15 %
Processing (melt) temperature			240 to 280 °C
Mold temperature			80 to 90 °C
Injection speed			中等偏快

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/Bf	215 °C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/Af	200 °C
Vicat softening temperature		ISO 306/B50	210 °C
Melting temperature		ISO 11357-3	220 °C

Physical properties	Test Condition	Test Method	Test Result
density		ISO 1183	1.35 g/cm³
Shrinkage rate	横向Flow	ISO 294-4	0.80 %
Shrinkage rate	Shrinkage rate	Flow	ISO 294-4	0.30 %
Water absorption rate	Saturation, 23°C, 2.00 mm	ISO 62	7.5 %
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 2.00 mm, 50% RH	ISO 62	2.0 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	1.0E+12 ohms
Volume resistivity		IEC 60093	1.0E+15 ohms·cm
Compared to the anti leakage trace index	Solution A	IEC 60112	PLC 1

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA6 RADILON® S RV300 RADIC ITALY

Material Description

Technical Data Sheet Compare

Technical Data Sheet