Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 S RV300 RADIC ITALY
RADILON®
--
High rigidity,Dimensional stability,Glass fiber reinforced,enhance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | RADIC ITALY/S RV300 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 11 kJ/m² |
| -30°C | ISO 179/1eA | 9.0 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 68 kJ/m² |
| -30°C | ISO 179/1eU | 60 kJ/m² |
| Mechanical properties | Test Condition | Test Method | RADIC ITALY/S RV300 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1A/1 | 9600 Mpa | |
| bending strength | ISO 178 | 245 Mpa | |
| Flexural modulus | ISO 178 | 8550 Mpa | |
| tensile strength | 断裂 | ISO 527-2/1A/5 | 175 Mpa |
| Tensile strain | 断裂 | ISO 527-2/1A/5 | 3.1 % |
| Electrical performance | Test Condition | Test Method | RADIC ITALY/S RV300 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1.0E+15 ohms·cm | |
| Compared to the Leakage Tracking Index (CTI) | 解决方案 A | IEC 60112 | PLC 1 |
| Surface Resistivity | IEC 60093 | 1.0E+12 ohms |
| flammability | Test Condition | Test Method | RADIC ITALY/S RV300 |
|---|---|---|---|
| Burning wire flammability index | 2.0 mm | IEC 60695-2-12 | 700 °C |
| flammability | 3.00 mm | FMVSS 302 | 0 mm/min |
| UL flame retardant rating | 0.8 mm | UL 94 | HB |
| physical property | Test Condition | Test Method | RADIC ITALY/S RV300 |
|---|---|---|---|
| Water absorption rate | 饱和, 23°C, 2.00 mm | ISO 62 | 7.5 % |
| 平衡, 23°C, 2.00 mm, 50% RH | ISO 62 | 2.0 % | |
| density | ISO 1183 | 1.35 g/cm³ | |
| Shrinkage rate | 流量 | ISO 294-4 | 0.30 % |
| 横向流量 | ISO 294-4 | 0.80 % |
| Thermal performance | Test Condition | Test Method | RADIC ITALY/S RV300 |
|---|---|---|---|
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/Bf | 215 °C |
| melting temperature | ISO 11357-3 | 220 °C | |
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/Af | 200 °C |
| vicat | ISO 306/B50 | 210 °C |
| injection | Test Condition | Test Method | RADIC ITALY/S RV300 |
|---|---|---|---|
| Suggested maximum moisture content | 0.15 % | ||
| Drying time - hot air dryer | 2.0 to 4.0 hr | ||
| Processing (melt) temperature | 240 to 280 °C | ||
| Dew Point - Hot Air Drying Machine | -20 °C | ||
| Temperature | 80 to 90 °C | ||
| injection speed | 中等偏快 | ||
| Drying temperature - hot air dryer | 80 °C |