PBT Crastin® S600F10 NC010 DuPont, European Union
187
- Unit Price:US$ 3,521 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:33MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:high viscosity
- Application Areas:Electronic and electrical components
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.50 mm | UL94 | HB |
| 3.00 mm | UL 94 | HB | |
| melting temperature | ISO 3146 | 225 ℃ | |
| Linear coefficient of thermal expansion | 平行流动方向，23 to 55℃ (73 to 130°F) | ISO 11359-1 | 0.00013 cm/cm/℃ |
| 垂直流动方向，23 to 55℃ (73 to 130°F) | ISO 11359-1 | 0.00013 cm/cm/℃ | |
| Heat Deflection Temperature | 0.45 Mpa，未退火 | ISO 75B-1 | 160 ℃ |
| 1.8Mpa，未退火 | ISO 75A-1 | 60 ℃ | |
| UL flame retardant rating | 0.750 mm | UL 94 | HB |
| Linear coefficient of thermal expansion | MD：-40to23°C | ISO 11359-2 | 8E-05 cm/cm/°C |
| MD：55to160°C | ISO 11359-2 | 1.9E-04 cm/cm/°C | |
| TD：-- | ISO 11359-2 | 1.2E-04 cm/cm/°C | |
| TD：-40to23°C | ISO 11359-2 | 9E-05 cm/cm/°C | |
| TD：55to160°C | ISO 11359-2 | 2E-04 cm/cm/°C | |
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 115 °C |
| 0.45MPa,退火 | ISO 75-2/B | 180 °C | |
| 1.8MPa,未退火 | ISO 75-2/A | 50.0 °C | |
| 1.8MPa,退火 | ISO 75-2/A | 60.0 °C | |
| Glass Transition Temperature | ISO 11357-2 | 55.0 °C | |
| vicat | ISO 306/B50 | 175 °C | |
| melting temperature | ISO 11357-3 | 224 °C | |
| Linear coefficient of thermal expansion | MD：-- | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| 3.0mm | UL 94 | HB | |
| 1.5mm | IEC 60695-11-10,-20 | HB | |
| 3.0mm | IEC 60695-11-10,-20 | HB | |
| Limiting Oxygen Index | ISO 4589-2 | 22 % | |
| FMVSS flammability | FMVSS302 | SE |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Emissions of Organic Compounds | VDA277 | 145 µgC/g | |
| Odor | VDA270 | 3.00 |
| Other performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Limiting Oxygen Index | ISO 4589-1 | 22 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 4.0 kJ/m² |
| 23°C | ISO 179/1eA | 5.0 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| 23°C | ISO 179/1eU | NoBreak | |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 5.0 kJ/m² |
| 23°C | ISO 180/1A | 5.0 kJ/m² | |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 130 kJ/m² |
| 23°C | ISO 180/1U | NoBreak |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | 23C/59RH | ISO 62 | 0.2 % |
| Sat/23C | ISO 62 | 0.5 % | |
| shrinkage rate | Across Flow | ISO 294-4 | 1.6 % |
| Flow | ISO 294-4 | 1.7 % | |
| density | ISO 1183 | 1.30 g/cm | |
| ISO 1183 | 1.30 g/cm³ | ||
| melt mass-flow rate | 250°C/2.16kg | ISO 1133 | 10 g/10min |
| shrinkage rate | TD | ISO 294-4 | 1.7 % |
| MD | ISO 294-4 | 1.7 % | |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 0.50 % |
| 平衡,23°C,2.00mm,50%RH | ISO 62 | 0.20 % | |
| MediumDensity | 1.11 g/cm³ | ||
| Ejection Temperature | 170 °C | ||
| SpecificHeatCapacity of Melt | 2100 J/kg/°C | ||
| ThermalConductivityofMelt | 0.21 W/m/K |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 1E+15 ohms | |
| volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| dielectric strength | -- | IEC 60243-1 | 26 KV/mm |
| 1.00mm3 | IEC 60243-1 | 26 KV/mm | |
| 2.00mm4 | IEC 60243-1 | 15 KV/mm | |
| relative permittivity | 100Hz | IEC 60250 | 3.60 |
| 1MHz | IEC 60250 | 3.20 | |
| Dissipation Factor | 100Hz | IEC 60250 | 1E-03 |
| 1MHz | IEC 60250 | 0.020 | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile stress | 23℃，屈服 | ISO 527-1 | 57 MPa |
| Tensile creep modulus | 1h | ISO 899-1 | 2600 MPa |
| 1000h | ISO 899-1 | 1800 MPa | |
| Tensile modulus | 23℃ | ISO 527-1 | 2700 MPa |
| bending strength | 23℃ | ISO 178 | 85 MPa |
| Impact strength of simply supported beam without notch | -30℃, Type 1, Edgewise | ISO 179 | No Break KJ/m |
| 23℃, Type 1, Edgewise | ISO 179 | No Break KJ/m | |
| Charpy Notched Impact Strength | -30 ℃, Type 1, Edgewise, Notch A | ISO 179 | 4 KJ/m |
| 23 ℃, Type 1, Edgewise, Notch A | ISO 179 | 5.4 KJ/m | |
| Suspended wall beam without notch impact strength | 23 ℃, Type 1 | ISO 180 | No Break KJ/m |
| Impact strength of cantilever beam gap | 23 ℃, Type 1, Notch A | ISO 180 | 6.5 KJ/m |
| Tensile modulus | ISO 527-2 | 2600 Mpa | |
| tensile strength | 屈服 | ISO 527-2 | 57.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2 | 4.0 % |
| Nominal tensile fracture strain | ISO 527-2 | >50 % | |
| Tensile creep modulus | 1hr | ISO 899-1 | 2300 Mpa |
| 1000hr | ISO 899-1 | 1800 Mpa | |
| flexural modulus | ISO 178 | 2300 Mpa | |
| bending strength | ISO 178 | 85.0 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.