Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT S600F10 NC010 DuPont, European Union
Crastin®
Electronic and electrical components
high viscosity
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | DuPont, European Union/S600F10 NC010 |
|---|---|---|---|
| Limiting Oxygen Index | ISO 4589-1 | 22 % |
| Impact resistance | Test Condition | Test Method | DuPont, European Union/S600F10 NC010 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 130 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 5.0 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 4.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 5.0 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | NoBreak |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 5.0 kJ/m² |
| Supplementary Information | Test Condition | Test Method | DuPont, European Union/S600F10 NC010 |
|---|---|---|---|
| Odor | VDA270 | 3.00 | |
| Emissions of Organic Compounds | VDA277 | 145 µgC/g |
| Mechanical properties | Test Condition | Test Method | DuPont, European Union/S600F10 NC010 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2600 Mpa | |
| bending strength | 23℃ | ISO 178 | 85 MPa |
| Impact strength of cantilever beam gap | 23 ℃, Type 1, Notch A | ISO 180 | 6.5 KJ/m |
| Tensile stress | 23℃，屈服 | ISO 527-1 | 57 MPa |
| Tensile creep modulus | 1000h | ISO 899-1 | 1800 MPa |
| Tensile strain | 屈服 | ISO 527-2 | 4.0 % |
| Tensile creep modulus | 1000hr | ISO 899-1 | 1800 Mpa |
| Charpy Notched Impact Strength | -30 ℃, Type 1, Edgewise, Notch A | ISO 179 | 4 KJ/m |
| Tensile creep modulus | 1hr | ISO 899-1 | 2300 Mpa |
| Tensile modulus | 23℃ | ISO 527-1 | 2700 MPa |
| Nominal tensile fracture strain | ISO 527-2 | >50 % | |
| Tensile creep modulus | 1h | ISO 899-1 | 2600 MPa |
| Impact strength of simply supported beam without notch | -30℃, Type 1, Edgewise | ISO 179 | No Break KJ/m |
| bending strength | ISO 178 | 85.0 Mpa | |
| Flexural modulus | ISO 178 | 2300 Mpa | |
| Impact strength of simply supported beam without notch | 23℃, Type 1, Edgewise | ISO 179 | No Break KJ/m |
| Suspended wall beam without notch impact strength | 23 ℃, Type 1 | ISO 180 | No Break KJ/m |
| Charpy Notched Impact Strength | 23 ℃, Type 1, Edgewise, Notch A | ISO 179 | 5.4 KJ/m |
| tensile strength | 屈服 | ISO 527-2 | 57.0 Mpa |
| Electrical performance | Test Condition | Test Method | DuPont, European Union/S600F10 NC010 |
|---|---|---|---|
| dielectric strength | 2.00mm4 | IEC 60243-1 | 15 KV/mm |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| relative permittivity | 100Hz | IEC 60250 | 3.60 |
| Dissipation Factor | 100Hz | IEC 60250 | 1E-03 |
| dielectric strength | 1.00mm3 | IEC 60243-1 | 26 KV/mm |
| -- | IEC 60243-1 | 26 KV/mm | |
| relative permittivity | 1MHz | IEC 60250 | 3.20 |
| Surface Resistivity | IEC 60093 | 1E+15 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.020 |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| flammability | Test Condition | Test Method | DuPont, European Union/S600F10 NC010 |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | IEC 60695-11-10,-20 | HB |
| 3.0mm | UL 94 | HB | |
| 1.5mm | IEC 60695-11-10,-20 | HB | |
| FMVSS flammability | FMVSS302 | SE | |
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| Limiting Oxygen Index | ISO 4589-2 | 22 % |
| physical property | Test Condition | Test Method | DuPont, European Union/S600F10 NC010 |
|---|---|---|---|
| melt mass-flow rate | 250°C/2.16kg | ISO 1133 | 10 g/10min |
| Water absorption rate | Sat/23C | ISO 62 | 0.5 % |
| Shrinkage rate | Flow | ISO 294-4 | 1.7 % |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 0.50 % |
| density | ISO 1183 | 1.30 g/cm | |
| ISO 1183 | 1.30 g/cm³ | ||
| SpecificHeatCapacity of Melt | 2100 J/kg/°C | ||
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO 62 | 0.20 % |
| Shrinkage rate | TD | ISO 294-4 | 1.7 % |
| MD | ISO 294-4 | 1.7 % | |
| MediumDensity | 1.11 g/cm³ | ||
| Ejection Temperature | 170 °C | ||
| Shrinkage rate | Across Flow | ISO 294-4 | 1.6 % |
| Water absorption rate | 23C/59RH | ISO 62 | 0.2 % |
| ThermalConductivityofMelt | 0.21 W/m/K |
| Thermal performance | Test Condition | Test Method | DuPont, European Union/S600F10 NC010 |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD：55to160°C | ISO 11359-2 | 1.9E-04 cm/cm/°C |
| UL flame retardant rating | 3.00 mm | UL 94 | HB |
| Linear coefficient of thermal expansion | 垂直流动方向，23 to 55℃ (73 to 130°F) | ISO 11359-1 | 0.00013 cm/cm/℃ |
| TD：55to160°C | ISO 11359-2 | 2E-04 cm/cm/°C | |
| vicat | ISO 306/B50 | 175 °C | |
| UL flame retardant rating | 1.50 mm | UL94 | HB |
| Heat distortion temperature | 1.8Mpa，未退火，HDT | ISO 75A-1 | 60 ℃ |
| 0.45MPa,退火，HDT | ISO 75-2/B | 180 °C | |
| Glass Transition Temperature | ISO 11357-2 | 55.0 °C | |
| Linear coefficient of thermal expansion | TD：-- | ISO 11359-2 | 1.2E-04 cm/cm/°C |
| melting temperature | ISO 11357-3 | 224 °C | |
| ISO 3146 | 225 ℃ | ||
| Linear coefficient of thermal expansion | MD：-40to23°C | ISO 11359-2 | 8E-05 cm/cm/°C |
| TD：-40to23°C | ISO 11359-2 | 9E-05 cm/cm/°C | |
| Heat distortion temperature | 0.45 Mpa，未退火，HDT | ISO 75B-1 | 160 ℃ |
| Linear coefficient of thermal expansion | MD：-- | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| UL flame retardant rating | 0.750 mm | UL 94 | HB |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 115 °C |
| Linear coefficient of thermal expansion | 平行流动方向，23 to 55℃ (73 to 130°F) | ISO 11359-1 | 0.00013 cm/cm/℃ |
| Heat distortion temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 60.0 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 50.0 °C |