PA66 TECHNYL® A 60G1 V30 SOLVAY FRANCE
310
- Unit Price:US$ 4,418 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:101MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
+86 ********View
For more details, please contact the supplier!
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
impact performance | Test Condition | Test Method | Test Result |
---|---|---|---|
Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 9.5 kJ/m² |
23°C | ISO 179/1eA | 10 kJ/m² | |
Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 60 kJ/m² |
23°C | ISO 179/1eU | 60 kJ/m² | |
Impact strength of cantilever beam gap | 23°C | ASTM D256 | 85 J/m |
flammability | Test Condition | Test Method | Test Result |
---|---|---|---|
UL flame retardant rating | 0.8 mm | UL 94 | V-0 |
1.6 mm | UL 94 | V-0 | |
3.2 mm | UL 94 | V-0 | |
Burning wire flammability index | 0.8 mm | IEC 60695-2-12 | 960 °C |
1.6 mm | IEC 60695-2-12 | 960 °C | |
3.2 mm | IEC 60695-2-12 | 960 °C | |
Hot filament ignition temperature | 0.8 mm | IEC 60695-2-13 | 775 °C |
Extreme Oxygen Index | ISO 4589-2 | 33 % | |
European Railways Certifications | R22 | EN 45545-2 | HL3 |
R23 | EN 45545-2 | HL3 |
mechanical properties | Test Condition | Test Method | Test Result |
---|---|---|---|
Tensile modulus | 23°C | ISO 527-2/1A | 10200 Mpa |
tensile strength | Break, 23°C | ASTM D638 | 140 Mpa |
Break, 23°C | ISO 527-2/1A | 150 Mpa | |
elongation | Break, 23°C | ASTM D638 | 3.0 % |
Break, 23°C | ISO 527-2 | 2.3 % | |
Bending modulus | 23°C | ASTM D790 | 10000 Mpa |
bending strength | 23°C | ASTM D790 | 225 Mpa |
23°C | ISO 178 | 255 Mpa |
injection | Test Condition | Test Method | Test Result |
---|---|---|---|
drying temperature | 80 °C | ||
Suggested maximum moisture content | 0.20 % | ||
Temperature at the rear of the barrel | 265 to 275 °C | ||
Temperature in the middle of the barrel | 265 to 275 °C | ||
Temperature at the front of the material cylinder | 270 to 280 °C | ||
Mold temperature | 60 to 90 °C |
thermal performance | Test Condition | Test Method | Test Result |
---|---|---|---|
Hot deformation temperature | 1.8 MPa, Unannealed | ISO 75-2/Af | 245 °C |
Melting temperature | ISO 11357-3 | 263 °C |
Physical properties | Test Condition | Test Method | Test Result |
---|---|---|---|
density | ISO 1183/A | 1.46 g/cm³ | |
Shrinkage rate | 横向Flow | ISO 294-4 | 1.0 % |
Flow | ISO 294-4 | 0.35 % | |
Water absorption rate | 24 hr, 23°C | ISO 62 | 0.73 % |
Saturation, 23°C | ISO 62 | 4.3 % | |
Equilibrium, 23°C, 50% RH | ISO 62 | 1.8 % | |
Outdoor applicability | 全部 | UL 746C | f1 |
Thermogravimetric analysis (TGA) | 1%失重温度 | NF F16-101 | I3 |
Electrical performance | Test Condition | Test Method | Test Result |
---|---|---|---|
Volume resistivity | IEC 60093 | 6.0E+14 ohms·cm | |
Dielectric strength | 0.800 mm | IEC 60243-1 | 38 KV/mm |
Compared to the anti leakage trace index | Solution A | IEC 60112 | V |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.