Material Description

Material Properties:Easy to form｜Easy to demould
Application Areas:Electronic and Electrical Applications｜Lighting applications
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Dart impact	--	ISO 6603-2	6.00 J
Dart impact	Dart impact	23°C, Energy at Peak	ASTM D3763	24.0 J
Suspended wall beam without notch impact strength	23°C3	ISO 180/1U	44 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ASTM D4812	720 J/m

mechanical properties	Test Condition	Test Method	Test Result
Wear factor		ASTM D3702	2.2E+7 10^-8 mm³/N·m
Friction coefficient	Static	ASTM D3702	0.53
Friction coefficient	Friction coefficient	Dynamic	ASTM D3702	0.51
bending strength		ASTM D790	158 Mpa
Bending modulus	--	ISO 178	6400 Mpa
Bending modulus	Bending modulus	--	ASTM D790	6200 Mpa
elongation	Break	ISO 527-2	2.5 %
	elongation	Break	ASTM D638	2.8 %
		elongation	Yield	ISO 527-2	2.5 %
		elongation	elongation	Yield	ASTM D638	2.8 %
tensile strength	Break	ISO 527-2	104 Mpa
	tensile strength	Break	ASTM D638	103 Mpa
	tensile strength	tensile strength	Yield	ASTM D638	103 Mpa
Tensile modulus	--	ISO 527-2/1	6740 Mpa
Tensile modulus	Tensile modulus	--1	ASTM D638	6890 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			120 °C
drying time			4.0 hr
Suggested maximum moisture content			0.020 %
Temperature at the rear of the barrel			295 to 305 °C
Temperature in the middle of the barrel			310 to 320 °C
Temperature at the front of the material cylinder			320 to 330 °C
Processing (melt) temperature			305 to 325 °C
Mold temperature			80 to 110 °C
Back pressure			0.200 to 0.300 Mpa
Screw speed			30 to 60 rpm

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	143 °C
	Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span3	ISO 75-2/Bf	145 °C
		Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	141 °C
		Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span3	ISO 75-2/Af	141 °C
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	4.7E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	3.6E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	3.6E-5 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	24 hr, 50% RH	ASTM D570	0.10 %
Shrinkage rate	Flow : 24hr	ISO 294-4	0.36 %
	Shrinkage rate	横向Flow : 24hr	ISO 294-4	0.44 %
		Shrinkage rate	Across FlowFlow : 24hr	ASTM D955	0.30 - 0.50 %
		Shrinkage rate	Shrinkage rate	Flow : 24hr	ASTM D955	0.30 - 0.50 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.