Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC DFL-4534 BK SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Electronic and Electrical Applications,Lighting applications
Easy to form,Easy to demould
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/DFL-4534 BK |
|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距3 | ISO 75-2/Bf | 145 °C |
| 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 141 °C | |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距3 | ISO 75-2/Af | 141 °C | |
| 0.45 MPa, 未退火, 3.20 mm | ASTM D648 | 143 °C | |
| Linear coefficient of thermal expansion | 横向 : -40°C | ISO 11359-2 | 3.6E-5 cm/cm/°C |
| 横向 : -40 到 40°C | ASTM E831 | 3.6E-5 cm/cm/°C | |
| 流动 : -40 到 40°C | ASTM E831 | 4.7E-5 cm/cm/°C |
| mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/DFL-4534 BK |
|---|---|---|---|
| Bending modulus | -- | ISO 178 | 6400 Mpa |
| -- | ASTM D790 | 6200 Mpa | |
| bending strength | ASTM D790 | 158 Mpa | |
| elongation | 屈服 | ISO 527-2 | 2.5 % |
| 断裂 | ASTM D638 | 2.8 % | |
| 断裂 | ISO 527-2 | 2.5 % | |
| 屈服 | ASTM D638 | 2.8 % | |
| Friction coefficient | Static | ASTM D3702 | 0.53 |
| Dynamic | ASTM D3702 | 0.51 | |
| Tensile modulus | --1 | ASTM D638 | 6890 Mpa |
| -- | ISO 527-2/1 | 6740 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 103 Mpa |
| 断裂 | ASTM D638 | 103 Mpa | |
| 断裂 | ISO 527-2 | 104 Mpa | |
| Wear factor | ASTM D3702 | 2.2E+7 10^-8 mm³/N·m |
| Physical properties | Test Condition | Test Method | SABIC INNOVATIVE US/DFL-4534 BK |
|---|---|---|---|
| Shrinkage rate | 横向流动 : 24小时 | ASTM D955 | 0.30 - 0.50 % |
| 流量 : 24小时 | ISO 294-4 | 0.36 % | |
| 横向流量 : 24小时 | ISO 294-4 | 0.44 % | |
| 流动 : 24小时 | ASTM D955 | 0.30 - 0.50 % | |
| Water absorption rate | 24 hr, 50% RH | ASTM D570 | 0.10 % |
| impact performance | Test Condition | Test Method | SABIC INNOVATIVE US/DFL-4534 BK |
|---|---|---|---|
| Dart impact | 23°C, Energy at Peak | ASTM D3763 | 24.0 J |
| -- | ISO 6603-2 | 6.00 J | |
| Suspended wall beam without notch impact strength | 23°C3 | ISO 180/1U | 44 kJ/m² |
| 23°C | ASTM D4812 | 720 J/m |
| injection | Test Condition | Test Method | SABIC INNOVATIVE US/DFL-4534 BK |
|---|---|---|---|
| Back pressure | 0.200 to 0.300 Mpa | ||
| drying temperature | 120 °C | ||
| drying time | 4.0 hr | ||
| Mold temperature | 80 to 110 °C | ||
| Processing (melt) temperature | 305 to 325 °C | ||
| Screw speed | 30 to 60 rpm | ||
| Suggested maximum moisture content | 0.020 % | ||
| Temperature at the front of the material cylinder | 320 to 330 °C | ||
| Temperature at the rear of the barrel | 295 to 305 °C | ||
| Temperature in the middle of the barrel | 310 to 320 °C |