PCTG

PCTG Tritan™ 401 EASTMAN USA

413

Unit Price:US$ 2,680 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
70MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Easy to process｜heat-resisting
Application Areas:Household daily necessities｜Electrical applications
Color:--
Grade:High gloss level

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
transmissivity	Total	ASTM D1003	92.0 %
turbidity	--2	Internal Method	<1.0 %
turbidity	turbidity	--	ASTM D1003	<1.0 %

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	-40°C	ASTM D256	130 J/m
	Impact strength of cantilever beam gap	23°C	ASTM D256	650 J/m
		Impact strength of cantilever beam gap	23°C3	Internal Method	640 J/m
			Impact strength of cantilever beam gap	23°C2	Internal Method	650 J/m
				Impact strength of cantilever beam gap	-40°C	ISO 180	14 kJ/m²
					Impact strength of cantilever beam gap	23°C	ISO 180	66 kJ/m²
						Impact strength of cantilever beam gap	-40°C	ASTM D4812	NoBreak
						Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D4812	NoBreak
Dart impact	-40°C,EnergyatMaxLoad	ASTM D3763	63.0 J
Dart impact	Dart impact	23°C,EnergyatMaxLoad	ASTM D3763	59.0 J

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	23°C	ASTM D638	1590 Mpa
Tensile modulus	Tensile modulus	23°C	ISO 527-2	1620 Mpa
tensile strength	Yield,23°C	ASTM D638	44.0 Mpa
	tensile strength	Yield,23°C2	Internal Method	44.0 Mpa
		tensile strength	Yield,23°C3	Internal Method	45.0 Mpa
			tensile strength	Yield,23°C	ISO 527-2	45.0 Mpa
				tensile strength	Break,23°C	ASTM D638	53.0 Mpa
				tensile strength	tensile strength	Break,23°C	ISO 527-2	49.0 Mpa
elongation	Yield,23°C2	Internal Method	7.0 %
	elongation	Yield,23°C3	Internal Method	6.5 %
	elongation	elongation	Yield,23°C	ASTM D638	7.0 %
Tensile strain	Yield,23°C	ISO 527-2	7.0 %
elongation	Break,23°C	ASTM D638	140 %
Tensile strain	Break,23°C	ISO 527-2	130 %
Bending modulus	23°C	ASTM D790	1590 Mpa
Bending modulus	Bending modulus	23°C	ISO 178	1530 Mpa
bending strength	Yield,23°C	ASTM D790	66.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	109 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	92.0 °C

Physical properties	Test Condition	Test Method	Test Result
density		ASTM D792	1.17 g/cm³
Shrinkage rate	MD：BlowMolded	Internal Method	1.2-1.6 %
Shrinkage rate	Shrinkage rate	MD：Injection	ASTM D955	0.50-0.70 %

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Sale,23°C	ASTM D785	115

Supplementary Information	Test Condition	Test Method	Test Result
Shrinkage rate	Boiling,1hr	Internal Method	<1.0 %
	Shrinkage rate	Boiling,2hr	Internal Method	<1.5 %
	Shrinkage rate	Shrinkage rate	Dishwasher	Internal Method	<1.0 %
MicrowaveBoiling-OvenPower		Internal Method	<2200 Watts
MicrowaveSteamSterilization-TotalEnergy		Internal Method	<11200 W-min
ThermalShock-WaterImmersion	35to98°C	Internal Method	Noeffect

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PCTG Tritan™ 401 EASTMAN USA

Material Description

Technical Data Sheet Compare

Technical Data Sheet