MABS

MABS 950-X02 TORAY JAPAN

473

Unit Price:US$ 2,826 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
30MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Detergent resistant｜Scratch resistant
Application Areas:Electrical applications｜OA device｜electrical equipment
Color:--
Grade:--

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
turbidity	3000μm	ISO 14782	3.0 %
transmissivity	Total,3000μm	ISO 13468	86.0 %

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C,3.20mm	ASTM D256	180 J/m
Charpy Notched Impact Strength	23°C	ISO 179	14 kJ/m²
Impact strength of cantilever beam gap	23°C,12.7mm	ASTM D256	170 J/m

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
bending strength	23°C	ISO 178	71.0 Mpa
bending strength	bending strength		ASTM D790	67.0 Mpa
Bending modulus	23°C	ISO 178	2180 Mpa
Bending modulus	Bending modulus		ASTM D790	2100 Mpa
Tensile strain	Break,23°C	ISO 527-2	14 %
elongation	Break	ASTM D638	20 %
tensile strength	Yield,23°C	ISO 527-2	50.0 Mpa
tensile strength	tensile strength		ASTM D638	43.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Vicat softening temperature			80.0to85.0 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	75.0 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	79.0 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate		Internal Method	0.40-0.60 %
melt mass-flow rate	220°C/10.0kg	ISO 1133	18 g/10min
density	23°C	ISO 1183	1.09 g/cm³
density	density		ASTM D792	1.09 g/cm³

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Sale,23°C	ISO 2039-2	110
Rockwell hardness	Rockwell hardness	R-Sale,23°C	ASTM D785	110

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

MABS 950-X02 TORAY JAPAN

Material Description

Technical Data Sheet Compare

Technical Data Sheet