PC LEXAN™ HF500R-73243 SABIC INNOVATIVE US
124
- Unit Price:US$ 2,432 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:20MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:enhance｜Glass fiber reinforced｜Filler: Glass fiber reinforced material｜9.0% filler by weight
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt volume flow rate | ISO 1133 | 16.0 cm3/10min | |
| Shrinkage rate | 内部方法 | 0.20-0.60 % | |
| Water absorption rate | ISO 62 | 0.31 % | |
| ISO 62 | 0.13 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 115 Mpa |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 | |
| Burning wire flammability index | IEC 60695-2-12 | 960 °C | |
| Limiting Oxygen Index | ISO 4589-2 | 35 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 3300 Mpa | |
| tensile strength | ISO 527-2/5 | 60.0 Mpa | |
| ISO 527-2/5 | 45.0 Mpa | ||
| Tensile strain | ISO 527-2/5 | 5.0 % | |
| ISO 527-2/5 | 7.0 % | ||
| Flexural modulus | ISO 178 | 3400 Mpa | |
| bending strength | ISO 178 | 95.0 Mpa | |
| Taber abraser | 内部方法 | 11.0 mg |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | 7.0 kJ/m² | |
| ISO 179/1eA | 8.0 kJ/m² | ||
| Impact strength of simply supported beam without notch | ISO 179/1eU | 无断裂 | |
| ISO 179/1eU | 无断裂 | ||
| Impact strength of cantilever beam gap | ISO 180/1A | 7.0 kJ/m² | |
| ISO 180/1A | 8.0 kJ/m² | ||
| Suspended wall beam without notch impact strength | ISO 180/1U | 110 kJ/m² | |
| ISO 180/1U | 无断裂 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| dielectric strength | IEC 60243-1 | 33 KV/mm | |
| IEC 60243-1 | 25 KV/mm | ||
| IEC 60243-1 | 16 KV/mm | ||
| relative permittivity | IEC 60250 | 2.90 | |
| IEC 60250 | 2.90 | ||
| IEC 60250 | 2.80 | ||
| Dissipation Factor | IEC 60250 | 1E-03 | |
| IEC 60250 | 1E-03 | ||
| IEC 60250 | 0.010 | ||
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ball-indentation hardness | IEC 60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 4E-05 cm/cm/°C | |
| thermal conductivity | ISO 8302 | 0.21 W/m/K | |
| RTI Elec | UL 746 | 130 °C | |
| RTI Imp | UL 746 | 125 °C | |
| RTI | UL 746 | 125 °C | |
| 0.45MPa, Unanealed, 100mm span | ISO 75-2/Be | 140 °C | |
| 1.8MPa, Unanealed, 100mm span | ISO 75-2/Ae | 132 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.