PC HF500R-73243 SABIC INNOVATIVE US
LEXAN™
--
enhance、Glass fiber reinforced、Filler: Glass fiber reinf、9.0% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/HF500R-73243 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 110 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 8.0 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 7.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 7.0 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 无断裂 |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 8.0 kJ/m² |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE US/HF500R-73243 |
|---|---|---|---|
| ball-indentation hardness | H358/30 | ISO 2039-1 | 115 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/HF500R-73243 |
|---|---|---|---|
| relative permittivity | 60Hz | IEC 60250 | 2.90 |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 | |
| dielectric strength | 0.800mm,在油中 | IEC 60243-1 | 33 KV/mm |
| relative permittivity | 50Hz | IEC 60250 | 2.90 |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| dielectric strength | 1.60mm,在油中 | IEC 60243-1 | 25 KV/mm |
| 3.20mm,在油中 | IEC 60243-1 | 16 KV/mm | |
| relative permittivity | 1MHz | IEC 60250 | 2.80 |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| Dissipation Factor | 50Hz | IEC 60250 | 1E-03 |
| 60Hz | IEC 60250 | 1E-03 | |
| 1MHz | IEC 60250 | 0.010 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/HF500R-73243 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 3300 Mpa | |
| tensile strength | 屈服 | ISO 527-2/5 | 60.0 Mpa |
| 断裂 | ISO 527-2/5 | 45.0 Mpa | |
| Tensile strain | 屈服 | ISO 527-2/5 | 5.0 % |
| bending strength | ISO 178 | 95.0 Mpa | |
| Flexural modulus | ISO 178 | 3400 Mpa | |
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | 内部方法 | 11.0 mg |
| Tensile strain | 断裂 | ISO 527-2/5 | 7.0 % |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/HF500R-73243 |
|---|---|---|---|
| UL flame retardant rating | 1.50mm | UL 94 | V-0 |
| Burning wire flammability index | 1.00mm | IEC 60695-2-12 | 960 °C |
| Limiting Oxygen Index | ISO 4589-2 | 35 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/HF500R-73243 |
|---|---|---|---|
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 16.0 cm3/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.13 % |
| 饱和,23°C | ISO 62 | 0.31 % | |
| Shrinkage rate | MD1 | 内部方法 | 0.20-0.60 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/HF500R-73243 |
|---|---|---|---|
| thermal conductivity | ISO 8302 | 0.21 W/m/K | |
| 0.45MPa, Unanealed, 100mm span | ISO 75-2/Be | 140 °C | |
| 1.8MPa, Unanealed, 100mm span | ISO 75-2/Ae | 132 °C | |
| Linear coefficient of thermal expansion | MD：23到80°C | ISO 11359-2 | 4E-05 cm/cm/°C |
| RTI Imp | UL 746 | 125 °C | |
| RTI | UL 746 | 125 °C | |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |
| RTI Elec | UL 746 | 130 °C |