ABS

ABS TAITALAC® 3100 TAIDA TAIWAN

329

Unit Price:US$ 2,442 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details
Material Comparison:
PC/ABS YF2300 NC HUIZHOU YOUFU

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Ultra high impact resistance type｜Widely used for extrusion molding/injection molding｜Ultra high impact strength｜Good processability｜Excellent hot forming
Application Areas:Used for luggage｜Toolbox｜Locomotive parts｜Low temperature products｜Helmet｜Bus box｜heel｜Controlled pipe fittings｜ etc｜Application in the automotive field｜Footwear
Color:--
Grade:Heat resistant grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C,6.35mm	ASTM D256	450 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,3.18mm	ASTM D256	490 J/m

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.6mm	UL 94	HB

Basic Performance	Test Condition	Test Method	Test Result
melt mass-flow rate	200℃/5kg	ASTM D-1238	0.8 g/10min
melt mass-flow rate	melt mass-flow rate	200℃/5kg	ASTM D-1238	8.0 g/10min
density		ASTM D-792	1.03
Water absorption rate		ASTM D-570	0.3 wt%

mechanical properties	Test Condition	Test Method	Test Result
flexural coefficient	23℃ 2.8mm/min	ASTM D-790	20000 kg/cm
flexural coefficient	flexural coefficient	23℃ 2.8mm/min	ASTM D-790	290000 psi
Rockwell hardness			100
Impact strength of cantilever beam gap	23℃1/2"	ASTM D-256	38 (7.0) kg.cm/cm(ft.1b/in)
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23℃1/8"	ASTM D-256	53 (9.8) kg.cm/cm(ft.1b/in)
tensile strength	23℃，Yield	ASTM D-638	350 kg/cm
	tensile strength	23℃，Yield	ASTM D-638	5000 psi
		tensile strength	1/8"，Break	ASTM D-638	4300 kg/cm
		tensile strength	tensile strength	1/8"，Break	ASTM D-638	300 psi
Elongation at Break	1/8"	ASTM D-638	50 %
bending strength	23℃ 2.8mm/min	ASTM D-790	600 kg/cm
	bending strength	23℃ 2.8mm/min	ASTM D-790	8500 psi
	bending strength	bending strength	Yield,23°C	ASTM D790	58.6 Mpa
Bending modulus	23°C	ASTM D790	2000 Mpa
elongation	Break,23°C,3.18mm	ASTM D638	90 %
tensile strength	Yield,23°C,3.18mm	ASTM D638	32.4 Mpa
tensile strength	tensile strength	Break,23°C,3.18mm	ASTM D638	27.6 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	Unannealed	ASTM D-1525	85(185) ℃(F)
Vicat softening temperature		ASTM D-1525	100 °C
UL flame retardant rating		UL 94	HB
Vicat softening temperature		ASTM D15254	102 °C
Hot deformation temperature	1.8MPa,Unannealed,12.7mm	ASTM D648	85.0 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate		ASTM D-955	0.4 %
melt mass-flow rate	200°C/5.0kg	ASTM D1238	0.80 g/10min
melt mass-flow rate	melt mass-flow rate	220°C/10.0kg	ASTM D1238	8.0 g/10min
Shrinkage rate	MD	ASTM D955	<0.40 %
density		ASTM D792	1.03 g/cm³
Water absorption rate	24hr	ASTM D570	<0.30 %

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Sale,23°C	ASTM D785	100

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

ABS TAITALAC® 3100 TAIDA TAIWAN

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet